Properties
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Processing Information (Sheet Extrusion)
- Impact Properties
- Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
| Value | Units | Test Method / Conditions | |
| Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 86 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 50 mm/min) ¹¹ | 73 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 50 mm/min) ¹¹ | 6 | % | ASTM D638 |
| Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 15 | % | ASTM D638 |
| Tensile Modulus (at 50 mm/min) ¹¹ | 3000 | MPa | ASTM D638 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 144 | MPa | ASTM D790 |
| Flexural Stress (Yield, 2.6 mm/min, 100 mm span) ¹¹ | 136 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 3150 | MPa | ASTM D790 |
| Flexural Modulus (at 2.6 mm/min, 100 mm span) ¹¹ | 2940 | MPa | ASTM D790 |
| Value | Units | Test Method / Conditions | |
| Specific Gravity ¹¹ | 1.08 | — | ASTM D792 |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.6 - 0.9 | % | SABIC method |
| Value | Units | Test Method / Conditions | |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 173 | °C | ASTM D1525 |
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 160 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 151 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ | 151 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.000063 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.0000558 | 1/°C | ASTM E831 |
| Value | Units | Test Method / Conditions | |
| Adapter Temperature | 240 - 265 | °C | — |
| Barrel - Zone 1 Temperature | 205 - 225 | °C | — |
| Barrel - Zone 2 Temperature | 215 - 240 | °C | — |
| Barrel - Zone 3 Temperature | 240 - 265 | °C | — |
| Barrel - Zone 4 Temperature | 240 - 265 | °C | — |
| Die Temperature | 240 - 265 | °C | — |
| Drying Temperature | 70 - 80 | °C | — |
| Drying Time | 2 - 4 | Hrs | — |
| Drying Time (Cumulative) | 8 | Hrs | — |
| Maximum Moisture Content | 0 | % | — |
| Melt Temperature | 265 - 275 | °C | — |
| Roll Stack Temperature - Bottom | 105 - 120 | °C | — |
| Roll Stack Temperature - Middle | 105 - 120 | °C | — |
| Roll Stack Temperature - Top | 105 - 120 | °C | — |
| Value | Units | Test Method / Conditions | |
| Izod Impact (Notched, at 23°C) ¹¹ | 32 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy (at 23°C) ¹¹ | 6 | J | ASTM D3763 |