NORYL™ Resin PX138H

Identification & Functionality

Fillers Included

Glass Fiber

Polymer Name

PPO/PS Alloy

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Blends & Alloys

Features & Benefits

Labeling Claims

No Added PFAS

Materials Features

Amorphous,

Dimensional Stability,

Excellent Stiffness,

Good Stiffness,

High Hydrolytic Stability,

High Stiffness,

High Strength,

Low Moisture Absorption,

Low Shrinkage,

Low Specific Gravity,

Low Warpage,

No Added PFAS

Applications & Uses

Markets

Building & Construction

Applications

Building & Construction — Building Envelope & Roofing

Glazing & Window Elements

Building & Construction — Building Materials

Interior Fixtures,

Pipes & Plumbing

Plastics & Elastomers End Uses

Building Materials,

Construction Applications,

Faucet System Components,

Fittings,

Gears,

Hoses,

Pipes,

Pump Parts,

Water Management

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Flame Rating

UL 94 HB

Physical Properties

	Value	Units	Test Method / Conditions
Mold Shrinkage (on Tensile Bar, flow) ᵍ ¹¹	0.2 - 0.4	%	SABIC method
Density ¹¹	1.25	g/cm³	ISO 1183
Density ¹¹	1.23	g/cm³	ISO 1183
Water Absorption (at 23°C, saturated) ¹¹	0.2	%	ISO 62-1
Water Absorption (at 23°C, saturated) ¹¹	0.12	%	ISO 62-1
Moisture Absorption (at 23°C, 50% RH) ¹¹	0.04	%	ISO 62
Moisture Absorption (at 23°C, 50% RH) ¹¹	0.06	%	ISO 62
Melt Volume Rate (at 280°C, 10.0 kg) ¹¹	15	cm³/10 min	ISO 1133
Specific Gravity ¹¹	1.23	—	ASTM D792
Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹	0.45 - 0.55	%	SABIC method
Melt Flow Rate (at 280°C, 5.0 kgf) ¹¹	2.7	g/10 min	ASTM D1238
Melt Volume Rate (at 280°C, 5.0 kg) ¹¹	2	cm³/10 min	ISO 1133

Mechanical Properties

	Value	Units	Test Method / Conditions
Taber Abrasion (CS-17, 1 kg) ¹¹	60	mg/1000cy	SABIC method
Tensile Stress (Yield, Type I, 5 mm/min) ¹¹	100	MPa	ASTM D638
Tensile Stress (Break, Type I, 5 mm/min) ¹¹	100	MPa	ASTM D638
Tensile Stress (Yield, 5 mm/min) ¹¹	90	MPa	ISO 527
Tensile Stress (Yield, 5 mm/min) ¹¹	80	MPa	ISO 527
Tensile Strain (Yield, Type I, 5 mm/min) ¹¹	3	%	ASTM D638
Tensile Stress (Break, 5 mm/min) ¹¹	90	MPa	ISO 527
Tensile Stress (Break, 5 mm/min) ¹¹	80	MPa	ISO 527
Tensile Strain (Break, Type I, 5 mm/min) ¹¹	3	%	ASTM D638
Tensile Strain (Yield, 5 mm/min) ¹¹	3	%	ISO 527
Tensile Strain (Yield, 5 mm/min) ¹¹	2.5	%	ISO 527
Tensile Modulus (at 5 mm/min) ¹¹	6500	MPa	ASTM D638
Tensile Strain (Break, 5 mm/min) ¹¹	2.5	%	ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹	3	%	ISO 527
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹	140	MPa	ASTM D790
Tensile Modulus (at 1 mm/min) ¹¹	6000	MPa	ISO 527
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹	5300	MPa	ASTM D790
Flexural Stress (Break, 2 mm/min) ¹¹	120	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	5400	MPa	ISO 178
Flexural Modulus (at 2 mm/min) ¹¹	4500	MPa	ISO 178
Ball Indentation Hardness (H358/30) ¹¹	100	MPa	ISO 2039-1
Flexural Stress (Yield, at 2 mm/min) ¹¹	150	MPa	ISO 178

Thermal Properties

	Value	Units	Test Method / Conditions
Thermal Conductivity ¹¹	0.26	W/m-°C	ISO 8302
Coefficient of Thermal Expansion (at 23°C to 80°C, flow) ¹¹	0.00003	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at 23°C to 80°C, xflow) ¹¹	0.00007	1/°C	ISO 11359-2
Vicat Softening Temperature (Rate A/50) ¹¹	145	°C	ISO 306
Vicat Softening Temperature (Rate B/50) ¹¹	143	°C	ASTM D1525
Vicat Softening Temperature (Rate B/50) ¹¹	143	°C	ISO 306
Vicat Softening Temperature (Rate B/50) ¹¹	135	°C	ISO 306
Vicat Softening Temperature (Rate B/120) ¹¹	140	°C	ISO 306
Vicat Softening Temperature (Rate B/120) ¹¹	147	°C	ISO 306
Heat Deflection Temperature/Be (at 0.45MPa, Edgew 120*10*4, sp=100mm) ¹¹	130	°C	ISO 75/Be
Heat Deflection Temperature/Ae (at 1.8 Mpa, Edgew 120*10*4, sp=100mm) ¹¹	120	°C	ISO 75/Ae
Relative Temperature Index (Electrical) ᵖ ¹¹	65	°C	UL 746B
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹	65	°C	UL 746B
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹	65	°C	UL 746B
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	137	°C	ASTM D648
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.000027	1/°C	ASTM E831
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹	0.000034	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.000075	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹	0.000082	1/°C	ASTM E831
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹	135	°C	ISO 75/Af

Electrical Properties

	Value	Units	Test Method / Conditions
Volume Resistivity ¹¹	1.00E+15	Ω.cm	IEC 60093
Surface Resistivity (ROA) ¹¹	min. 1.E15	Ω	IEC 60093
Dielectric Strength (in oil, at 3.2mm) ¹¹	18	kV/mm	IEC 60243-1
Relative Permittivity (1 MHz) ¹¹	2.9	—	IEC 60250
Dissipation Factor (at 50/60 Hz) ¹¹	0.0008	—	IEC 60250
Dissipation Factor (at at 1 MHz) ¹¹	0.003	—	IEC 60250
Comparative Tracking Index ʳ ¹¹	250	V	IEC 60112
Relative Permittivity (50/60 Hz) ¹¹	2.9	—	IEC 60250
Comparative Tracking Index (UL, PLC) ¹¹	5	PLC Code	UL 746A

Impact Properties

	Value	Units	Test Method / Conditions
Charpy Impact (at -30°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹	25	kJ/m²	ISO 179/1eU
Charpy Impact (at 23°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹	25	kJ/m²	ISO 179/1eU
Izod Impact (Unnotched, 80*10*4, at -30°C) ¹¹	23	kJ/m²	ISO 180/1U
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹	23	kJ/m²	ISO 180/1U
Izod Impact (Notched, at 23°C) ¹¹	90	J/m	ASTM D256
Izod Impact (Notched, at -30°C) ¹¹	100	J/m	ASTM D256
Instrumented Dart Impact Total Energy (at 23°C) ¹¹	20	J	ASTM D3763
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹	30	kJ/m²	ISO 180/1A
Izod Impact (Notched, 80*10*4, at -30°C) ¹¹	33	kJ/m²	ISO 180/1A
Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹	8	kJ/m²	ISO 179/1eA

Injection Molding

	Value	Units	Test Method / Conditions
Drying Temperature ⁷	100 - 120	°C	—
Drying Temperature ⁷	110 - 120	°C	—
Drying Time (Cumulative) ⁷	8	Hrs	—
Drying Time (Cumulative) ⁷	2 - 3	Hrs	—
Melt Temperature ⁷	280 - 300	°C	—
Melt Temperature ⁷	300 - 325	°C	—
Nozzle Temperature ⁷	260 - 280	°C	—
Nozzle Temperature ⁷	300 - 325	°C	—
Front - Zone 3 Temperature ⁷	280 - 300	°C	—
Front - Zone 3 Temperature ⁷	290 - 325	°C	—
Middle - Zone 2 Temperature ⁷	260 - 280	°C	—
Middle - Zone 2 Temperature ⁷	275 - 320	°C	—
Rear - Zone 1 Temperature ⁷	240 - 260	°C	—
Rear - Zone 1 Temperature ⁷	265 - 315	°C	—
Hopper Temperature ⁷	60 - 80	°C	—
Mold Temperature ⁷	80 - 110	°C	—
Mold Temperature ⁷	80 - 120	°C	—
Drying Time ⁷	3 - 4	Hrs	—
Maximum Moisture Content ⁷	0.02	%	—
Back Pressure ⁷	0.3 - 0.7	MPa	—
Screw Speed ⁷	20 - 100	rpm	—
Shot to Cylinder Size ⁷	30 - 70	%	—

Flame Characteristics

	Value	Units	Test Method / Conditions
UL Recognized (94HB Flame Class Rating) ᵖ	min. 1.5	mm	UL 94
UL Recognized (94HB Flame Class Rating) ᵖ	1.5	mm	UL 94
Glow Wire Flammability Index (passes at 750°C) ʳ ᵖ	3.2	mm	IEC 60695-2-12
Oxygen Index (LOI) ᵖ	26	%	ISO 4589

Note

• ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
• ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
• ʳ UL Ratings shown on the technical datasheet might not cover the full range of thicknesses, colors and regions. For details, please see the UL Yellow Card.
• ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
• ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

 

Regulatory & Compliance

Certifications & Compliance