Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
Features & Benefits
- Materials Features
- Potential Benefits of LEXAN EXL Resin
- Impact: Best-in-class ductility to -60 ºC with an outstanding balance of ductility and viscosity.
- Weatherability: Excellent retention of mechanical properties upon outdoor exposure.
- Aging: Better retention of properties vs. other polycarbonate resins.
- Flame retardance: FR grades can be used in many ECO-compliant applications.
- Knitline strength: A significant improvement over PC/ABS material
- Chemical resistance: Improved chemical resistance to some chemicals compared to standard polycarbonate
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Color
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Impact Properties
- Injection Molding
- Note
- ʰ Measurements made from laboratory test coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
| Value | Units | Test Method / Conditions | |
| Tensile Stress (Yield, Type I, 5 mm/min) ¹¹ | 55 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 46 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 5 mm/min) ¹¹ | 4.5 | % | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 19 | % | ASTM D638 |
| Tensile Modulus (at 5 mm/min) ¹¹ | 3300 | MPa | ASTM D638 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 105 | MPa | ASTM D790 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 2850 | MPa | ASTM D790 |
| Tensile Stress (Yield, 5 mm/min) ¹¹ | 55 | MPa | ISO 527 |
| Tensile Stress (Break, 5 mm/min) ¹¹ | 47 | MPa | ISO 527 |
| Tensile Strain (Yield, 5 mm/min) ¹¹ | 4.6 | % | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 15.4 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 3200 | MPa | ISO 527 |
| Flexural Stress (Yield, at 2 mm/min) ¹¹ | 104 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 2830 | MPa | ISO 178 |
| Value | Units | Test Method / Conditions | |
| Specific Gravity ¹¹ | 1.22 | — | ASTM D792 |
| Mold Shrinkage (flow, 3.2 mm) ʰ ¹¹ | 0.2 - 0.6 | % | SABIC method |
| Melt Flow Rate (at 300°C, 1.2 kgf) ¹¹ | 6.6 | g/10 min | ASTM D1238 |
| Density ¹¹ | 1.22 | g/cm³ | ISO 1183 |
| Water Absorption (at 23°C, saturated) ¹¹ | 0.12 | % | ISO 62-1 |
| Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.46 | % | ISO 62 |
| Melt Volume Rate (at 300°C, 1.2 kg) ¹¹ | 6 | cm³/10 min | ISO 1133 |
| Value | Units | Test Method / Conditions | |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 146 | °C | ASTM D1525 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 146 | °C | ISO 306 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 137 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.000048 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.000048 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.000071 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.000071 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature (Rate B/120) ¹¹ | 148 | °C | ISO 306 |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 134 | °C | ISO 75/Af |
| Value | Units | Test Method / Conditions | |
| Izod Impact (Notched, at 23°C) ¹¹ | 260 | J/m | ASTM D256 |
| Izod Impact (Notched, at -30°C) ¹¹ | 166 | J/m | ASTM D256 |
| Instrumented Dart Impact Total Energy (at 23°C) ¹¹ | 39 | J | ASTM D3763 |
| Izod Impact (Unnotched, 80*10*3, at 23°C) ¹¹ | No break | kJ/m² | ISO 180/1U |
| Izod Impact (Unnotched, 80*10*3, at -30°C) ¹¹ | No break | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*3, at 23°C) ¹¹ | 30 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*3, at -30°C) ¹¹ | 10 | kJ/m² | ISO 180/1A |
| Charpy Impact (at 23°C, V-notch Edgew 80*10*3 sp=62mm) ¹¹ | 25 | kJ/m² | ISO 179/1eA |
| Charpy Impact (at -30°C, V-notch Edgew 80*10*3 sp=62mm) ¹¹ | 15 | kJ/m² | ISO 179/1eA |
| Charpy Impact (at 23°C, Unnotch Edgew 80*10*3 sp=62mm) ¹¹ | No break | kJ/m² | ISO 179/1eU |
| Charpy Impact (at -30°C, Unnotch Edgew 80*10*3 sp=62mm) ¹¹ | No break | kJ/m² | ISO 179/1eU |
| Value | Units | Test Method / Conditions | |
| Drying Temperature ⁷ | 120 | °C | — |
| Drying Time ⁷ | 3 - 4 | Hrs | — |
| Drying Time (Cumulative) ⁷ | 48 | Hrs | — |
| Maximum Moisture Content ⁷ | 0.02 | % | — |
| Melt Temperature ⁷ | 310 - 330 | °C | — |
| Nozzle Temperature ⁷ | 305 - 325 | °C | — |
| Front - Zone 3 Temperature ⁷ | 310 - 330 | °C | — |
| Middle - Zone 2 Temperature ⁷ | 300 - 320 | °C | — |
| Rear - Zone 1 Temperature ⁷ | 290 - 310 | °C | — |
| Mold Temperature ⁷ | 80 - 115 | °C | — |
| Back Pressure ⁷ | 0.3 - 0.7 | MPa | — |
| Screw Speed ⁷ | 40 - 70 | rpm | — |
| Shot to Cylinder Size ⁷ | 40 - 60 | % | — |
| Vent Depth ⁷ | 0.025 - 0.076 | mm | — |
Packaging & Availability
- Regional Availability