Properties
- Flame Rating
- Physical Properties
- Mechanical Properties
- Thermal Properties
- Electrical Properties
- Impact Properties
- Injection Molding
- Flame Characteristics
- Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
- ʳ UL Ratings shown on the technical datasheet might not cover the full range of thicknesses, colors and regions. For details, please see the UL Yellow Card.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
| Value | Units | Test Method / Conditions | |
| Density ¹¹ | 1.18 | g/cm³ | ISO 1183 |
| Density ¹¹ | 1.16 | g/cm³ | ISO 1183 |
| Density ¹¹ | 1.162 | g/cm³ | ASTM D792 |
| Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ | 0.5 | % | ASTM D570 |
| Moisture Absorption (at 23°C, 50% RH, 24hrs) ¹¹ | 0.19 | % | ISO 62-4 |
| Moisture Absorption (at 23°C, 50% RH, Equilibrium) ¹¹ | 0.56 | % | ISO 62-4 |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 0.77 | % | ISO 62-1 |
| Water Absorption (at 23°C, 24hrs) ¹¹ | 0.77 | % | ASTM D570 |
| Water Absorption (at 23°C, saturated) ¹¹ | 2.12 | % | ISO 62-1 |
| Water Absorption (at 23°C, saturated) ¹¹ | 2.12 | % | ASTM D570 |
| Water Absorption (at 23°C, saturated) ¹¹ | 3.3 | % | ISO 62-1 |
| Melt Volume Rate (at 280°C, 5.0 kg) ¹¹ | 11 | cm³/10 min | ISO 1133 |
| Melt Volume Rate (at 280°C, 5.0 kg) ¹¹ | 8 | cm³/10 min | ISO 1133 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.66 | % | ISO 294 |
| Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹ | 0.66 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 0.99 | % | ASTM D955 |
| Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹ | 0.99 | % | ISO 294 |
| Specific Gravity ¹¹ | 1.16 | — | ASTM D792 |
| Melt Flow Rate (at 280°C, 5.0 kgf) ¹¹ | 12 | g/10 min | ASTM D1238 |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.6 - 0.8 | % | SABIC method |
| Moisture Absorption (at 50% RH, Equilibrium) ¹¹ | 1 | % | ASTM D570 |
| Mold Shrinkage (xflow, 3.2 mm) ᵍ ¹¹ | 0.7 - 1 | % | SABIC method |
| Mold Shrinkage (xflow, 3.2 mm) ᵍ ¹¹ | 0.65 - 0.85 | % | SABIC method |
| Mold Shrinkage (on Tensile Bar, flow) ᵍ ¹¹ | 0.6 - 1 | % | SABIC method |
| Moisture Absorption (at 23°C, 50% RH) ¹¹ | 1.11 | % | ISO 62 |
| Value | Units | Test Method / Conditions | |
| Tensile Modulus (at 1 mm/min) ¹¹ | 3200 | MPa | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 4200 | MPa | ISO 527 |
| Tensile Stress (Yield, 5 mm/min) ¹¹ | 65 | MPa | ISO 527 |
| Tensile Stress (Yield, 5 mm/min) ¹¹ | 102 | MPa | ISO 527 |
| Tensile Stress (Yield, Type I, 5 mm/min) ¹¹ | 96 | MPa | ASTM D638 |
| Tensile Stress (Yield, Type I, 5 mm/min) ¹¹ | 89 | MPa | ASTM D638 |
| Tensile Stress (Break, 5 mm/min) ¹¹ | 65 | MPa | ISO 527 |
| Tensile Stress (Break, 5 mm/min) ¹¹ | 95 | MPa | ISO 527 |
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 88 | MPa | ASTM D638 |
| Tensile Stress (Break, Type I, 5 mm/min) ¹¹ | 91 | MPa | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 10 | % | ASTM D638 |
| Tensile Strain (Break, Type I, 5 mm/min) ¹¹ | 5.5 | % | ASTM D638 |
| Tensile Strain (Yield, 5 mm/min) ¹¹ | 3.5 | % | ISO 527 |
| Tensile Strain (Yield, 5 mm/min) ¹¹ | 3.9 | % | ISO 527 |
| Flexural Stress (Yield, 2.6 mm/min, 100 mm span) ¹¹ | 155 | MPa | ASTM D790 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 6 | % | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 5.2 | % | ISO 527 |
| Flexural Modulus (at 2.6 mm/min, 100 mm span) ¹¹ | 3960 | MPa | ASTM D790 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 2900 | MPa | ISO 178 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 3900 | MPa | ISO 178 |
| Flexural Stress (Break, 2 mm/min) ¹¹ | 105 | MPa | ISO 178 |
| Flexural Stress (Break, 2 mm/min) ¹¹ | 163 | MPa | ISO 178 |
| Hardness (Rockwell R) ¹¹ | 119 | — | ASTM D785 |
| Flexural Stress (Yield, at 2 mm/min) ¹¹ | 165 | MPa | ISO 178 |
| Ball Indentation Hardness (H358/30) ¹¹ | 90 | MPa | ISO 2039-1 |
| Tensile Modulus (at 5 mm/min) ¹¹ | 4050 | MPa | ASTM D638 |
| Tensile Strain (Yield, Type I, 5 mm/min) ¹¹ | 4 | % | ASTM D638 |
| Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹ | 3950 | MPa | ASTM D790 |
| Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹ | 158 | MPa | ASTM D790 |
| Value | Units | Test Method / Conditions | |
| Heat Deflection Temperature/Bf (at 0.45 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 241 | °C | ISO 75/Bf |
| Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹ | 192 | °C | ISO 75/Af |
| Vicat Softening Temperature (Rate A/50) ¹¹ | 250 | °C | ISO 306 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 240 | °C | ASTM D1525 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 200 | °C | ISO 306 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 221 | °C | ISO 306 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 221 | °C | ASTM D1525 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 0.00006 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 0.000044 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹ | 0.000044 | 1/°C | ASTM E831 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹ | 0.00008 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹ | 0.000087 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹ | 0.000087 | 1/°C | ASTM E831 |
| Heat Deflection Temperature (at 0.45 MPa, 3.2 mm, Unannealed) ¹¹ | 239 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹ | 201 | °C | ASTM D648 |
| Heat Deflection Temperature (at 0.45 MPa, 6.4 mm, Unannealed) ¹¹ | 245 | °C | ASTM D648 |
| Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ | 210 | °C | ASTM D648 |
| Coefficient of Thermal Expansion (at -20°C to 150°C, flow) ¹¹ | 0.000039 - 0.00005 | 1/°C | ASTM E831 |
| Thermal Conductivity ¹¹ | 0.24 | W/m-°C | ISO 8302 |
| Ball Pressure Test (at 123°C to 127°C) ¹¹ | Pass | — | IEC 60695-10-2 |
| Vicat Softening Temperature (Rate B/120) ¹¹ | 205 | °C | ISO 306 |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 120 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 60 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 125 | °C | UL 746B |
| Value | Units | Test Method / Conditions | |
| High Voltage Arc Track Rate (PLC) ¹¹ | 3 | PLC Code | UL 746A |
| Comparative Tracking Index (UL, PLC) ¹¹ | 3 | PLC Code | UL 746A |
| High Ampere Arc Ignition (PLC 0) ¹¹ | min. 1.5 | mm | UL 746A |
| Hot Wire Ignition (PLC 0) ¹¹ | min. 1.5 | mm | UL 746A |
| Arc Resistance (Tungsten, PLC) ¹¹ | 6 | PLC Code | ASTM D495 |
| Value | Units | Test Method / Conditions | |
| Izod Impact (Notched, at 23°C) ¹¹ | 80 | J/m | ASTM D256 |
| Izod Impact (Notched, at -30°C) ¹¹ | 53 | J/m | ASTM D256 |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 85 | kJ/m² | ISO 180/1U |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 50 | kJ/m² | ISO 180/1U |
| Izod Impact (Unnotched, 80*10*4, at -30°C) ¹¹ | 40 | kJ/m² | ISO 180/1U |
| Charpy Impact (Notched, at 23°C) ¹¹ | 6 | kJ/m² | ISO 179/2C |
| Charpy Impact (Notched, at -20°C) ¹¹ | 4 | kJ/m² | ISO 179/2C |
| Charpy Impact (at 23°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹ | 60 | kJ/m² | ISO 179/1eU |
| Charpy Impact (at -30°C, Unnotch Edgew 80*10*4 sp=62mm) ¹¹ | 40 | kJ/m² | ISO 179/1eU |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 6.8 | kJ/m² | ISO 180/1A |
| Charpy Impact (at 23°C, V-notch Edgew 80*10*4 sp=62mm) ¹¹ | 6.5 | kJ/m² | ISO 179/1eA |
| Izod Impact (Unnotched, at 23°C) ¹¹ | 740 | J/m | ASTM D4812 |
| Value | Units | Test Method / Conditions | |
| Drying Temperature ⁷ | 100 - 110 | °C | — |
| Drying Temperature ⁷ | 95 - 105 | °C | — |
| Drying Time ⁷ | 3 - 4 | Hrs | — |
| Drying Time ⁷ | 2 - 3 | Hrs | — |
| Drying Time (Cumulative) ⁷ | 8 | Hrs | — |
| Maximum Moisture Content ⁷ | 0.07 | % | — |
| Melt Temperature ⁷ | 280 - 305 | °C | — |
| Melt Temperature ⁷ | 280 - 300 | °C | — |
| Minimum Moisture Content ⁷ | 0.02 | % | — |
| Nozzle Temperature ⁷ | 280 - 305 | °C | — |
| Nozzle Temperature ⁷ | 270 - 290 | °C | — |
| Front - Zone 3 Temperature ⁷ | 280 - 300 | °C | — |
| Front - Zone 3 Temperature ⁷ | 275 - 305 | °C | — |
| Middle - Zone 2 Temperature ⁷ | 270 - 290 | °C | — |
| Middle - Zone 2 Temperature ⁷ | 270 - 305 | °C | — |
| Rear - Zone 1 Temperature ⁷ | 260 - 280 | °C | — |
| Rear - Zone 1 Temperature ⁷ | 265 - 305 | °C | — |
| Hopper Temperature ⁷ | 60 - 80 | °C | — |
| Mold Temperature ⁷ | 80 - 100 | °C | — |
| Mold Temperature ⁷ | 75 - 120 | °C | — |
| Back Pressure ⁷ | 0.3 - 1.4 | MPa | — |
| Screw Speed ⁷ | 20 - 100 | rpm | — |
| Shot to Cylinder Size ⁷ | 30 - 50 | % | — |
| Vent Depth ⁷ | 0.013 - 0.038 | mm | — |
| Value | Units | Test Method / Conditions | |
| UL Recognized (94HB Flame Class Rating) ʳ | min. 1.5 | mm | UL 94 |
| Oxygen Index (LOI) ʳ | 26 | % | ISO 4589 |
Regulatory & Compliance
- Certifications & Compliance
Packaging & Availability
- Country Availability
- Regional Availability