Knowde Enhanced TDS
Identification & Functionality
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Flame Rating
- Physical Properties
- Mechanical Properties
- Thermal Properties
- Electrical Properties
- Impact Properties
- Injection Molding
- Flame Characteristics
- Note
- ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
- ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
- ⁵ For detailed processing conditions please contact the SABIC representative. Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
| Value | Units | Test Method / Conditions | |
| Mold Shrinkage (flow, 3.2 mm) ᵍ ¹¹ | 0.1 - 0.3 | % | SABIC method |
| Mold Shrinkage (xflow, 3.2 mm) ᵍ ¹¹ | 0.2 - 0.5 | % | SABIC method |
| Specific Gravity ¹¹ | 1.29 | — | ASTM D792 |
| Water Absorption (at 23°C, saturated) ¹¹ | 0.2 | % | ISO 62-1 |
| Density ¹¹ | 1.3 | g/cm³ | ISO 1183 |
| Moisture Absorption (at 23°C, 50% RH) ¹¹ | 0.06 | % | ISO 62 |
| Melt Volume Rate (at 300°C, 10.0 kg) ¹¹ | 16 | cm³/10 min | ISO 1133 |
| Value | Units | Test Method / Conditions | |
| Tensile Stress (Break, 5 mm/min) ¹¹ | 106 | MPa | ISO 527 |
| Tensile Strain (Break, 5 mm/min) ¹¹ | 2 | % | ISO 527 |
| Tensile Modulus (at 1 mm/min) ¹¹ | 8100 | MPa | ISO 527 |
| Flexural Stress (Break, 2 mm/min) ¹¹ | 170 | MPa | ISO 178 |
| Ball Indentation Hardness (H358/30) ¹¹ | 130 | MPa | ISO 2039-1 |
| Flexural Modulus (at 2 mm/min) ¹¹ | 7050 | MPa | ISO 178 |
| Taber Abrasion (CS-17, 1 kg) ¹¹ | 70 | mg/1000cy | SABIC method |
| Value | Units | Test Method / Conditions | |
| Ball Pressure Test (at 123°C to 127°C) ¹¹ | Pass | — | IEC 60695-10-2 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹ | 0.00002 | 1/°C | ISO 11359-2 |
| Coefficient of Thermal Expansion (at -40°C to 40°C, xflow) ¹¹ | 0.00007 | 1/°C | ISO 11359-2 |
| Vicat Softening Temperature (Rate A/50) ¹¹ | 155 | °C | ISO 306 |
| Vicat Softening Temperature (Rate B/50) ¹¹ | 149 | °C | ISO 306 |
| Vicat Softening Temperature (Rate B/120) ¹¹ | 158 | °C | ISO 306 |
| Heat Deflection Temperature/Be (at 0.45MPa, Edgew 120*10*4, sp=100mm) ¹¹ | 145 | °C | ISO 75/Be |
| Heat Deflection Temperature/Ae (at 1.8 Mpa, Edgew 120*10*4, sp=100mm) ¹¹ | 140 | °C | ISO 75/Ae |
| Relative Temperature Index (Electrical) ᵖ ¹¹ | 65 | °C | UL 746B |
| Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 65 | °C | UL 746B |
| Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 65 | °C | UL 746B |
| Value | Units | Test Method / Conditions | |
| Dielectric Strength (in oil, at 3.2mm) ¹¹ | 18 | kV/mm | IEC 60243-1 |
| Dissipation Factor (at 50/60 Hz) ¹¹ | 0.0006 | — | IEC 60250 |
| Dissipation Factor (at at 1 MHz) ¹¹ | 0.001 | — | IEC 60250 |
| Relative Permittivity (1 MHz) ¹¹ | 2.9 | — | IEC 60250 |
| Relative Permittivity (50/60 Hz) ¹¹ | 2.9 | — | IEC 60250 |
| Surface Resistivity (ROA) ¹¹ | min. 1.E+15 | Ω | IEC 60093 |
| Volume Resistivity ¹¹ | 1.00E+15 | Ω.cm | IEC 60093 |
| Value | Units | Test Method / Conditions | |
| Multi-Axial Impact (at 23°C) ¹¹ | 6 | J | ISO 6603 |
| Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹ | 34 | kJ/m² | ISO 180/1U |
| Izod Impact (Unnotched, 80*10*4, at -30°C) ¹¹ | 30 | kJ/m² | ISO 180/1U |
| Izod Impact (Notched, 80*10*4, at 23°C) ¹¹ | 11 | kJ/m² | ISO 180/1A |
| Izod Impact (Notched, 80*10*4, at -30°C) ¹¹ | 10 | kJ/m² | ISO 180/1A |
| Value | Units | Test Method / Conditions | |
| Drying Temperature ⁵ | 100 - 120 | °C | — |
| Drying Time ⁵ | 2 - 4 | Hrs | — |
| Maximum Moisture Content ⁵ | 0.02 | % | — |
| Melt Temperature ⁵ | 280 - 300 | °C | — |
| Nozzle Temperature ⁵ | 280 - 300 | °C | — |
| Front - Zone 3 Temperature ⁵ | 290 - 310 | °C | — |
| Middle - Zone 2 Temperature ⁵ | 270 - 290 | °C | — |
| Rear - Zone 1 Temperature ⁵ | 250 - 270 | °C | — |
| Hopper Temperature ⁵ | 60 - 80 | °C | — |
| Mold Temperature ⁵ | 80 - 120 | °C | — |
| Value | Units | Test Method / Conditions | |
| UL Recognized (94HB Flame Class Rating) ᵖ | min. 1.5 | mm | UL 94 |
| Oxygen Index (LOI) ᵖ | 26 | % | ISO 4589 |
| Glow Wire Flammability Index (passes at 750°C) ᵖ | 3 | mm | IEC 60695-2-12 |
| Glow Wire Ignitability Temperature (at 3.0 mm) ᵖ | 750 | °C | IEC 60695-2-13 |
Regulatory & Compliance
- Certifications & Compliance
Packaging & Availability
- Regional Availability