Knowde Enhanced TDS
Identification & Functionality
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
Applications & Uses
- Markets
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Flame Rating
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Electrical Properties
- Impact Properties
- Injection Molding
- Flame Characteristics
- Note
- ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
- ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
- ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
Value | Units | Test Method / Conditions | |
Tensile Stress (Yield, Type I, 50 mm/min) ¹¹ | 73 | MPa | ASTM D638 |
Tensile Strain (Break, Type I, 50 mm/min) ¹¹ | 14 | % | ASTM D638 |
Flexural Stress (Yield, 2.6 mm/min, 100 mm span) ¹¹ | 100 | MPa | ASTM D790 |
Flexural Modulus (at 2.6 mm/min, 100 mm span) ¹¹ | 2500 | MPa | ASTM D790 |
Value | Units | Test Method / Conditions | |
Specific Gravity ¹¹ | 1.1 | — | ASTM D792 |
Melt Flow Rate (at 250°C, 10.0 kgf) ¹¹ | 5 | g/10 min | ASTM D1238 |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature (at 1.82 MPa, 6.4 mm, Unannealed) ¹¹ | 118 | °C | ASTM D648 |
Ball Pressure Test (approximate maximum) ¹¹ | 120 | °C | IEC 60695-10-2 |
Relative Temperature Index (Electrical) ᵖ ¹¹ | 125 | °C | UL 746B |
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹ | 125 | °C | UL 746B |
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹ | 125 | °C | UL 746B |
Value | Units | Test Method / Conditions | |
Dielectric Strength (in air, at 3.2mm) ¹¹ | 27 | kV/mm | ASTM D149 |
Comparative Tracking Index (UL, PLC) ¹¹ | 2 | PLC Code | UL 746A |
Hot Wire Ignition (PLC 1) ¹¹ | min. 3 | mm | UL 746A |
Value | Units | Test Method / Conditions | |
Izod Impact (Notched, at 23°C) ¹¹ | 180 | J/m | ASTM D256 |
Value | Units | Test Method / Conditions | |
Drying Temperature ⁷ | 105 - 110 | °C | — |
Drying Time ⁷ | 3 - 4 | Hrs | — |
Drying Time (Cumulative) ⁷ | 8 | Hrs | — |
Maximum Moisture Content ⁷ | 0.02 | % | — |
Melt Temperature ⁷ | 275 - 305 | °C | — |
Nozzle Temperature ⁷ | 275 - 305 | °C | — |
Front - Zone 3 Temperature ⁷ | 265 - 305 | °C | — |
Middle - Zone 2 Temperature ⁷ | 255 - 300 | °C | — |
Rear - Zone 1 Temperature ⁷ | 245 - 295 | °C | — |
Mold Temperature ⁷ | 70 - 100 | °C | — |
Back Pressure ⁷ | 0.3 - 0.7 | MPa | — |
Screw Speed ⁷ | 20 - 100 | rpm | — |
Shot to Cylinder Size ⁷ | 30 - 70 | % | — |
Vent Depth ⁷ | 0.038 - 0.051 | mm | — |
Value | Units | Test Method / Conditions | |
UL Recognized (94V-0 Flame Class Rating) ᵖ | min. 0.75 | mm | UL 94 |