Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
- Key Features
- Impact Resistance
- High Strength
- Temperature Resistance
- Key Features
- High Mechanical Properties
- Low Temperature Conditions Remain High Impact Resistance And Mechanical Properties
- Low Warp
- High Rigidity
- Good Ductility
- High Rigidity
- Benefits and Advantage
- High Temperature Resistance, Corrosion Resistance, Dimensional Stability And Accuracy, Good Metal Substitute Material
- High Dimensional Accuracy, Precision Molding, V-0 Ul94 Flame Retardant Grade, Low Voc, Low Water Absorption, Weld Seam Strength High, Cost-Effective
Applications & Uses
- Markets
- Plastics & Elastomers Processing Methods
- Typical Applications
Can be used in the production of Aluminum Alloy fixture, mixing warter valve, water heater set of water treatment equipment, and other products in the field of high toughness
Properties
- Mechanical Properties
- Thermal Properties
- Typical Properties
- Electrical Properties
- Processing Parameters
| Value | Units | Test Method / Conditions | |
| Tensile Strength | 190 | mPa | ISO 527 |
| Elongation at Break | 2 | % | ISO 527 |
| Flexural Modulus | 13 | GPa | ISO 178 |
| Flexural Strength | 280 | mPa | ISO178 |
| Charpy Impact Strength (V-notched) | 14 | kJ/m² | IS0 179 |
| Value | Units | Test Method / Conditions | |
| Melting temperature (10°C/min) | 280 | °C | ISO 11357 |
| Heat Deflection Tem p High Load (1.8MPa) | 260 | °C | ISO 75 |
| Flammability | V-0 | class | UL-94 |
| Value | Units | Test Method / Conditions | |
| Density | 1630 | kg/m³ | ISO 1183 |
| Mold shrinkage (Machine Direction) | 0.2 | % | GB/T 15585 |
| Mold shrinkage (Transverse Direction) | 0.7 | % | GB/T 15585 |
| Water Absorption (23°C-sat) | 0.02 | % | ISO 62 |
| Value | Units | Test Method / Conditions | |
| Dielectric Strength | 16 | KV/mm | IEC 60243 |
| Dielectric Constant | 4 | - | IEC 60250 |
| Dissipation Factor | 0.002 | - | IEC 60250 |
| Volume Resistivity | 2×10^15 | Ω.cm | IEC 60093 |
| CTI | 150 | V | IEC 60112 |
| Value | Units | Test Method / Conditions | |
| Drying at 3h | 150 | °C | - |
| Injection Pressure | 30~100 | mPa | - |
| Injection Molding Melt Temperature | 290~330 | °C | ISO 294 |
| Injection Molding Melt Temperature | 120~160 | °C | ISO 294 |
| Limit in-cylinder retention time at 300°C | min. 60 | - | - |
| Limit in-cylinder retention time at 300°C | min. 48 | - | - |
| Limit in-cylinder retention time at 300°C | min. 78 | - | - |