Features & Benefits
- Labeling Claims
- Materials Features
- Key Features
- Low Chlorine
- Excellent Mechanical Properties
- Good Electrical Properties And Chemical Resistance
Applications & Uses
- Applications
- Plastics & Elastomers Processing Methods
- Typical Applications
Can be used in electronics,communications,high-frequency heating industrial equipment and measurement, inspection and test equipment such as the need to engage in electrostatic and electromagnetic shielding and other occasions, in order to reduce the source magnetic radiation effect
Properties
- Mechanical Properties
- Thermal Properties
- Typical Properties
- Electrical Properties
- Processing Parameters
Value | Units | Test Method / Conditions | |
Tensile Strength | 165 | mPa | ISO 527 |
Elongation at Break | 1.6 | % | ISO 527 |
Flexural Modulus | 15 | GPa | ISO 178 |
Flexural Strength | 250 | mPa | ISO178 |
Charpy Impact Strength (V-notched) | 9 | kJ/m² | IS0 179 |
Value | Units | Test Method / Conditions | |
Melting temperature (10°C/min) | 280 | °C | ISO 11357 |
Heat Deflection Tem p High Load (1.8MPa) | 260 | °C | ISO 75 |
Flammability | V-0 | class | UL-94 |
Value | Units | Test Method / Conditions | |
Density | 1700 | kg/m³ | ISO 1183 |
Mold shrinkage (Machine Direction) | 0.2 | % | GB/T 15585 |
Mold shrinkage (Transverse Direction) | 0.65 | % | GB/T 15585 |
Water Absorption (23°C-sat) | 0.02 | % | ISO 62 |
Value | Units | Test Method / Conditions | |
Dielectric Strength | 16 | KV/mm | IEC 60243 |
Dielectric Constant | 4 | — | IEC 60250 |
Dissipation Factor | 0.002 | — | IEC 60250 |
Volume Resistivity | 2×10^15 | Ω.cm | IEC 60093 |
CTI | 155 | V | IEC 60112 |
Value | Units | Test Method / Conditions | |
Drying at 3h | 150 | °C | — |
Injection Pressure | 30~100 | mPa | — |
Injection Molding Melt Temperature | 290~330 | °C | ISO 294 |
Injection Molding Melt Temperature | 120~160 | °C | ISO 294 |
Limit in-cylinder retention time at 300°C | min. 60 | — | — |