Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
Features & Benefits
- Materials Features
- Key Features
- High Modulus
- High Stiffness
- Dimentional Stability
- Low Shrinkage And Warpage
- Good Electrical Properties
- High Temperature Dimensional Stability
- Suitable For Coating&Plating
- High Temperature Resistance
- High Rigidity
- Dimensional Stability
- Creep Resistance
- Low Warp Dimensional Stability
- Creep Resistance
- Benefits and Advantage
- Excellent Coating And Plating Properties, Heat Resistance, High Impact Resistance, High Rigidity, Excellent Electrical Properties, Low Density, Is A Good Substitute For Copper, Aluminum And Metal Alloy .
Applications & Uses
- Markets
- Plastics & Elastomers Processing Methods
- Typical Applications
Can be used in auto parts such as Fuel Pump Impellers,Reflector Housing,Socket Bases and other high temperature resistant parts.
Properties
- Mechanical Properties
- Thermal Properties
- Typical Properties
- Electrical Properties
- Processing Parameters
| Value | Units | Test Method / Conditions | |
| Tensile Strength | 155 | mPa | ISO 527 |
| Elongation at Break | 1.2 | % | ISO 527 |
| Flexural Modulus | 19 | GPa | ISO 178 |
| Flexural Strength | 245 | mPa | ISO178 |
| Charpy Impact Strength (V-notched) | 9 | kJ/m² | IS0 179 |
| Value | Units | Test Method / Conditions | |
| Melting temperature (10°C/min) | 280 | °C | ISO 11357 |
| Heat Deflection Tem p High Load (1.8MPa) | 260 | °C | ISO 75 |
| Flammability | V-0 | class | UL-94 |
| Value | Units | Test Method / Conditions | |
| Density | 1900 | kg/m³ | ISO 1183 |
| Mold shrinkage (Machine Direction) | 0.3 | % | GB/T 15585 |
| Mold shrinkage (Transverse Direction) | 0.6 | % | GB/T 15585 |
| Water Absorption (23°C-sat) | 0.02 | % | ISO 62 |
| Value | Units | Test Method / Conditions | |
| Dielectric Strength | 14 | KV/mm | IEC 60243 |
| Dielectric Constant | 5 | - | IEC 60250 |
| Dissipation Factor | 0.001 | - | IEC 60250 |
| Volume Resistivity | 1.6×10^15 | Ω.cm | IEC 60093 |
| CTI | 180 | V | IEC 60112 |
| Value | Units | Test Method / Conditions | |
| Drying at 3h | 150 | °C | - |
| Injection Pressure | 30~100 | mPa | - |
| Injection Molding Melt Temperature | 290~330 | °C | ISO 294 |
| Injection Molding Melt Temperature | 120~160 | °C | ISO 294 |
| Limit in-cylinder retention time at 300°C | min. 60 | - | - |
| Limit in-cylinder retention time at 300°C | min. 65 | - | - |
| Limit in-cylinder retention time at 300°C | min. 82 | - | - |