Crystic VE671-03 has excellent resistance to a wide range of chemical substances (acid, alkalies and oxidizing agents).
Applications & Uses
- Markets
- Composites Processing Methods
- Recommended Applications
Crystic VE671-03 was designed for use in closed mold applications and centrifugal casting processes. It is recommended for the manufacture of fiber reinforced composite tanks, vessels, ducts etc. for use in chemical processing applications.
- Formulation Guidelines
Crystic VE 671-03 should be allowed to attain workshop temperature (18°C-25°C) before use. It requires the addition of a catalyst and accelerators to start the curing reaction. The correct amount of Accelerator G (1% Cobalt) and Acetyl Acetone should be stirred into the resin. The recommended catalyst for this system is Trigonox 239, which should be added at 2% into the resin and thoroughly dispersed. The geltime can be adjusted by varying the levels of Acetyl Acetone.
Properties
- Mechanical Properties
- Typical Liquid Resin Properties
- Laminate Property
Laminate property
At different temperature Temperature (°C) 23°C 65°C 93°C 107°C 121°C 149°C Flexural strength (MPa) 208 198 189 101 34 22 Flexural modulus (GPa) 7.6 6.9 5.9 3.4 3.3 1.6 Tensile strength (MPa) 152 172 145 124 76 50 Tensile modulus (GPa) 9.9 10.2 8.5 6.3 4.3 - Compressive strength (MPa) 1185 - - - - - Glass content (%)
40 Laminate construction:
V/M/M/WR/M/WR/M V = veil, M = CSM, WR = woven roving
- Note
** Curing Schedule: 24 hrs at 20°C followed by 3 hrs at 80°C
*** Curing Schedule: 24 hrs at 20°C followed by 5 hrs at 80°C and then 3 hrs at 120°C
Value | Units | Test Method / Conditions | |
Tensile Strength** | 80 | MPa | BS or BS EN ISO test method |
Tensile Modulus** | 3.4 | GPa | BS or BS EN ISO test method |
Elongation (to break) ** | 4 - 5 | % | BS or BS EN ISO test method |
Flexural Strength** | 125 | MPa | BS or BS EN ISO test method |
Barcol Hardness** | 45 | — | BS or BS EN ISO test method |
Heat Deflection Temperature*** | 95 - 100 | °C | BS or BS EN ISO test method |
Water Absorption (7 days)** | 35 | mg | BS or BS EN ISO test method |
Value | Units | Test Method / Conditions | |
Acid Value | max. 8.5 | mg KOH/g | BS or BS EN ISO test method |
Viscosity (at 25°C, Brookfield RVT) | 150 - 200 | mPa.s | BS or BS EN ISO test method |
Color | max. 7 | Gardner | BS or BS EN ISO test method |
Volatile Content | 51 - 55 | % | BS or BS EN ISO test method |
Gel Time (at 25°C, using 2% Acc.G & 2% Trigonox 239) | 20 - 30 | Minutes | BS or BS EN ISO test method |
Gel Time (at 25°C, using 2% Acc.G 0.06 % Acetyl acetone & 2% Trigonox 239) | 110 | Minutes | BS or BS EN ISO test method |
Technical Details & Test Data
- Post Curing
Satisfactory laminates for many applications can be made from Crystic VE671-03 by curing at workshop temperature (20°C). However, for optimum properties and long term performance laminates must be post cured before being put into service. Moldings should be allowed to cure for 24 hours at 20°C and then be oven cured for a minimum of 3 hours at 80°C. Post curing at 100°C is advisable if moldings are to operate at high temperatures.
Packaging & Availability
- Packaging Type
- Regional Availability
- Packaging
- Crystic® VE 671-03 is supplied in 225kg drums.
Storage & Handling
- Shelf Life
- 6 Months
- Storage
- Crystic® VE 671-03 should be stored in the dark in suitable closed containers. It is recommended that the storage temperature should be less than 20°C where practical, but should not exceed 30°C.