NBR 1845 is essentially an acrylonitrile (17-20%) and 1,3-butadiene copolymer obtained by emulsion polymerization method with the use of fatty acid soaps as emulsifier in accordance with the ecologically clean technology. Low content of acrylonitrile, good frost-resistance, satisfactory oil resistance.

NBR 2675 is essentially an acrylonitrile (27-30%) and 1,3-butadiene copolymer obtained by emulsion polymerization method with the use of fatty acid soaps as emulsifier in accordance with the ecologically clean technology. Medium content of acrylonitrile, heightened oil resistance.

Synthetic rubber SBR-1502 is styrene (23.5%) and butadiene (76.5%) copolymer obtained by cold emulsion polymerization using the soaps of resin and fatty

Butadiene-methylstyrene synthetic rubber SBR-1723 TDAE is essentially a product of copolymerization of butadiene with α-methylstyrene in emulsion at a temperature of (4-8) °C where complex emulsifiers based on fatty acid and resin soaps are used. The rubber contains high -aromatic oil and stabilizers of amine-phenol type.

Styrene-butadiene synthetic rubber SSBR-3755 TDAE is the copolymerization product of 1,3-butadiene with styrene in hydrocarbon solvent in the presence of organolithium compounds and it is filled with TDAE oil and stabilized with staining antioxidant.

Synthetic styrene-butadiene rubber Styrene-butadiene synthetic rubber SSBR-4040 TDAE is the copolymerization product of 1,3-butadiene with styrene in hydrocarbon solvent in the presence of organolithium compounds and it is filled with TDAE oil and stabilized with staining antioxidant. The polymer contains no nitrosamines and substances that may become a source of nitrosamines.

It is a liquid, from light yellow to brown, with a characteristic smell of aromatic hydrocarbons. Guaranteed shelf life of products – 1 month from the date of manufacture.

Synthetic styrene-butadiene rubber is obtained by emulsion copolymerisation of butadiene with styrene and filled with TDAE oil

Synthetic cis-butadiene rubber BR-1243 Nd HV is a product of polymerization of butadiene in solution in the presence of rare-earth metal-base catalysts with addition of an antioxidant, which contains at least 97% of 1,4-cisbonds. The polymer contains no nitrosamines or substances that may be a source of nitrosamines.

IMPRAMER™ B 2247 bromobutyl rubber is a brominated copolymer of isobutylene and isoprene. Product is offered as white to light amber color bale and has 0.93 as typical specific gravity.

IMPRAMER™ B 2232 bromobutyl rubber is a brominated copolymer of isobutylene and isoprene. Product is offered as white to light amber color bale and has 0.93 as typical specific gravity.

Styrene butadiene synthetic rubber SBR-1502 is essentially a styrene (23.5%) and butadiene (76.5%) copolymer obtained by emulsification method with the use of resin/fatty soaps; non-staining antioxidant

Synthetic cis-butadiene rubber SIBUR BR-1245 is a product of polymerization of butadiene in solution in the presence of neodymium catalyst; 1,4-cis — at least 97%; polydispersity — no more 2.5. The polymer is stabilized by non- staining antioxidant and contains no nitrosamines or substances that may be a source of nitrosamines.

Synthetic cis-butadiene rubber SIBUR BR-1203 Ti is the polymerization product of butadiene in solution; in the presence of titanium catalyst; 1,4-cis – at least 90%. The polymer is stabilized with non-staining antioxidant and contains no nitrosamines or substances that may be a source of nitrosamines.

Synthetic styrene-butadiene rubber is obtained by emulsion copolymerisation of butadiene with styrene; filled with high aromatic petroleum oil and stabilized with staining antioxidant

Synthetic styrene-butadiene rubber Styrene-butadiene synthetic rubber SSBR-4040 TDAE is the copolymerization product of 1,3-butadiene with styrene in hydrocarbon solvent in the presence of organolithium compounds and it is filled with TDAE oil and stabilized with staining antioxidant. The polymer contains no nitrosamines and substances that may become a source of nitrosamines.

Styrene butadiene synthetic rubber SBR-1502 is essentially a styrene (23.5%) and butadiene (76.5%) copolymer obtained by emulsification method with the use of resin/fatty soaps.

NBR 3375 NT is essentially an acrylonitrile (31-35%) and 1,3-butadiene copolymer obtained by emulsion polymerization method with the use of fatty acid soaps as emulsifier in accordance with the ecologically clean technology. Medium content of acrylonitrile, heightened oil resistance.

Synthetic styrene-butadiene rubber is obtained by emulsion copolymerisation of butadiene with styrene and filled with high aromatic oil

NBR 3355 NT is essentially an acrylonitrile (31-35%) and 1,3-butadiene copolymer obtained by emulsion polymerization method with the use of fatty acid soaps as emulsifier in accordance with the ecologically clean technology. Medium content of acrylonitrile, heightened oil resistance.

Synthetic rubber SIBUR BR-1500 is styrene (23.5%) and butadiene (76.5%) copolymer obtained by cold emulsion polymerization using the soaps of resin and fatty acids. The polymer is stabilized with non-staining antioxidant and contains no nitrosamines and substances that may become a source of nitrosamines.

Synthetic styrene-butadiene rubber is obtained by emulsion copolymerisation of butadiene with styrene and filled with TDAE oil

Styrene butadiene synthetic rubber SBR-1500 is essentially a styrene (23.5%) and butadiene (76.5%) copolymer obtained by emulsification method with the use of resin/fatty soaps.

C5-C8 - for use as a solvent for paints and varnishes, to obtain light petroleum resins, aromatic hydrocarbons, which are used as raw materials for plastics and for processes of fine organic synthesis.

Heavy resins of pyrolysis is used in the production of carbon black, superplasticizers concretes, as a component of boiler fuel.

Synthetic acrylonitrile-butadiene rubber (content acrylonitrile 27-30 %) filled with polyvinylchloride (PVC) is obtained by joint coagulation of butadiene-acrylonitrile latex with polyvinylchloride latex.

NBR 4045 is essentially an acrylonitrile (36-40%) and 1,3-butadiene copolymer obtained by emulsion polymerization method with the use of fatty acid soaps as emulsifier in accordance with the ecologically clean technology. High content of acrylonitrile, very high oil resistance.

Synthetic acrylonitrile-butadiene rubber (content acrylonitrile 27-30 %) filled with polyvinylchloride (PVC) is obtained by joint coagulation of butadiene-acrylonitrile latex with polyvinylchloride latex.

Synthetic styrene-butadiene rubber is obtained by emulsion copolymerisation of butadiene with styrene and filled with high aromatic oil

NBR 2655 is essentially an acrylonitrile (27-30%) and 1,3-butadiene copolymer obtained by emulsion polymerization method with the use of fatty acid soaps as emulsifier in accordance with the ecologically clean technology. Medium content of acrylonitrile, heightened oil resistance.

Styrene butadiene synthetic rubber SBR-1500 is essentially a styrene (23.5%) and butadiene (76.5%) copolymer obtained by emulsification method with the use of resin/fatty soaps; non-staining antioxidant

NBR 2645 NT is essentially an acrylonitrile (27-30%) and 1,3-butadiene copolymer obtained by emulsion polymerization method with the use of fatty acid soaps as emulsifier in accordance with the ecologically clean technology. Medium content of acrylonitrile, heightened oil resistance.

Synthetic styrene-butadiene rubber / methylstyrene rubber is obtained by low-temperature emulsion copolymerisation of butadiene with styrene/methylstyrene and filled with petroleum-based softeners.

Synthetic rubber SBR-1502 is styrene (23.5%) and butadiene (76.5%) copolymer obtained by cold emulsion polymerization using the soaps of resin and fatty

Synthetic polybutadiene rubber Synthetic cis-butadiene rubber BR-1203 Ti is the polymerization product of butadiene in solution; in the presence of titanium catalyst; 1,4-cis – at least 90%. The polymer is stabilized with non-staining antioxidant and contains no nitrosamines or substances that may be a source of nitrosamines.

Styrene-butadiene synthetic rubber SSBR-2560 TDAE is the copolymerization product of 1,3-butadiene with styrene in hydrocarbon solvent in the presence of organolithium compounds and it is filled with TDAE oil and stabllized with staining antioxidant. The polymer contains по nitrosamines and substances that may become а source of nitrosamines.