Temperature Hardening Powder (% pbw.*) Pot life (approx. min.) Hardening time (approx. min.) 0°C 5 20 80 5°C 4 19 70 10°C 3 19 65 15°C 2 18 60 20°C 1.5 18 55 25°C - 35°C 1 12 50 * The quantity of hardening powder is always related to the quantity of resin including Additive I.
Properties
- Resin Properties
| Value | Units | Test Method / Conditions | |
| Viscosity (20°C) | max. 50 | mPa.s | DIN 53 015 |
| Flow Time (20°C, 4 mm Cup) | 25 - 30 | sec. | DIN 53 211 |
| Density (D₄²⁰) | 0.97 | g/cm³ | DIN 51 757 |
| Flash Point | 10.0 | °C | DIN 51 755 |
| Pot Life (20°C, 100 g, 3 % pbw. Hardening Powder) | approx. 18 min. | — | — |
| Application Temperature | 0 - 35 | °C | — |
| Density (Hardened state) | 1.12 | g/cm³ | DIN 53 479 |
| Ultimate Elongation (Hardened state) | 75.0 | % | DIN 53 455 |
| Hardness (Hardened state) | 40 - 45 | Shore-D | DIN 53 505 |
| Water Absorption (4 Days, Hardened State, 50·50·4 mm) | 125.0 | mg | DIN 53 495 |
| Modulus of elasticity | 205.0 | N/mm² | DIN 53 457 |
| Compressive Strength | 30.0 | N/mm² | DIN 1164 |
| Tensile Strength | 15.0 | N/mm² | DIN 1164 |
| Modulus of Elasticity | 1200.0 | N/mm² | DIN 53 457 |
Regulatory & Compliance
- Application
Layer thickness must be adjusted to the eveness of the concrete and to the mechanical loading and is recommended between 5 and 20 mm. Lower thickness must be avoided as the curing process will slow down. A higher thickness of more than 20 mm will cause shrinkage and tension. For a proper application mix hardener fi rst to the resin and add fi nally the fi ller mix. Normally there is no need to use pigments, however it could be an option.