Solaxis Nylon 11 - PA 11 - Polyamide - 3D Printing

Identification & Functionality

Chemical Family: Polyamides
Polymer Name: Polyamide 11 (PA 11)
Technologies: Plastics
Product Families: Plastics — 3D Printing Polymers
Other 3D Printing Polymers

Features & Benefits

Materials Features: High Elasticity,
High Elongation,
High Impact Resistance

Applications & Uses

Markets: Consumer Goods,
Industrial
Applications: Industrial — Chemical & Industrial Manufacturing
Tooling & Moldmaking
Consumer Goods — Other Consumer Goods Applications
Plastics & Elastomers End Uses: 3D Printing Applications,
Prototyping
Plastics & Elastomers Processing Methods: 3D Printing,
Selective Laser Sintering

Properties

Color: Black,
White
Mechanical Properties
Typical Properties
Thermal Properties

	Value	Units	Test Method / Conditions
Tensile Strength (Drying 14 days at 80°C / vacuum,X direction)	52	MPa	ISO 527-2 (23°C)
Tensile Strength (Drying 14 days at 80°C / vacuum,X direction)	32	MPa	ISO 527 -2 (80°C)
Tensile Modulus (Drying 14 days at 80°C / vacuum,X direction)	1750	MPa	ISO 527 -2 (23°C)
Tensile Modulus (Drying 14 days at 80°C / vacuum,X direction)	390	MPa	ISO 527 -2 (80°C)
Tensile Elongation at Break (Drying 14 days at 80°C / vacuum,X direction)	26	%	ISO 527 -2 (23°C)
Tensile Elongation at Break (Drying 14 days at 80°C / vacuum,X direction)	min. 150	%	ISO 527 -2 (80°C)
Flexural Modulus (Drying 14 days at 80°C / vacuum,X direction)	1750	MPa	DIN EN ISO 178
Charpy Impact Strength (notched,Drying 14 days at 80°C / vacuum,X direction)	7.6	kJ/m²	ISO 179 -1
Charpy Impact Strength (unnotched,Drying 14 days at 80°C / vacuum,X direction)	193	kJ/m²	ISO 179 -1
Izod Impact Strength (notched,Drying 14 days at 80°C / vacuum,X direction)	7.9	J/m	ISO 180
Izod Impact Strength (unnotched,Drying 14 days at 80°C / vacuum,X direction)	no break	J/m	ISO 180
Tensile Strength (Drying 14 days at 80°C / vacuum,Z direction)	52	MPa	ISO 527-2 (23°C)
Tensile Strength (Drying 14 days at 80°C / vacuum,Z direction)	28	MPa	ISO 527 -2 (80°C)
Tensile Modulus (Drying 14 days at 80°C / vacuum,Z direction)	1700	MPa	ISO 527 -2 (23°C)
Tensile Modulus (Drying 14 days at 80°C / vacuum,Z direction)	360	MPa	ISO 527 -2 (80°C)
Tensile Elongation at Break (Drying 14 days at 80°C / vacuum,Z direction)	27	%	ISO 527 -2 (23°C)
Tensile Elongation at Break (Drying 14 days at 80°C / vacuum,Z direction)	87	%	ISO 527 -2 (80°C)
Flexural Modulus (Drying 14 days at 80°C / vacuum,Z direction)	1700	MPa	DIN EN ISO 178
Charpy Impact Strength (notched,Drying 14 days at 80°C / vacuum,Z direction)	7.7	kJ/m²	ISO 179 -1
Charpy Impact Strength (unnotched,Drying 14 days at 80°C / vacuum,Z direction)	56	kJ/m²	ISO 179 -1
Izod Impact Strength (notched,Drying 14 days at 80°C / vacuum,Z direction)	8	J/m	ISO 180
Izod Impact Strength (unnotched,Drying 14 days at 80°C / vacuum,Z direction)	48	J/m	ISO 180
Tensile Strength (Conditioning 14 days at 70°C / 62% r.h. , X direction)	45	MPa	ISO 527-2 (23°C)
Tensile Strength (Conditioning 14 days at 70°C / 62% r.h. , X direction)	28	MPa	ISO 527 -2 (80°C)
Tensile Modulus (Conditioning 14 days at 70°C / 62% r.h. , X direction)	1150	MPa	ISO 527 -2 (23°C)
Tensile Modulus (Conditioning 14 days at 70°C / 62% r.h. , X direction)	330	MPa	ISO 527 -2 (80°C)
Tensile Elongation at Break (Conditioning 14 days at 70°C / 62% r.h. , X direction)	42	%	ISO 527 -2 (23°C)
Tensile Elongation at Break (Conditioning 14 days at 70°C / 62% r.h. , X direction)	min. 150	%	ISO 527 -2 (80°C)
Flexural Modulus (Conditioning 14 days at 70°C / 62% r.h. , X direction)	1300	MPa	DIN EN ISO 178
Charpy Impact Strength (notched,Conditioning 14 days at 70°C / 62% r.h. , X direction)	11	kJ/m²	ISO 179 -1
Charpy Impact Strength (unnotched,Conditioning 14 days at 70°C / 62% r.h. , X direction)	no break	kJ/m²	ISO 179 -1
Izod Impact Strength (notched,Conditioning 14 days at 70°C / 62% r.h. , X direction)	9.3	J/m	ISO 180
Izod Impact Strength (unnotched,Conditioning 14 days at 70°C / 62% r.h. , X direction)	no break	J/m	ISO 180
Tensile Strength (Conditioning 14 days at 70°C / 62% r.h. , Z direction)	45	MPa	ISO 527-2 (23°C)
Tensile Strength (Conditioning 14 days at 70°C / 62% r.h. , Z direction)	26	MPa	ISO 527 -2 (80°C)
Tensile Modulus (Conditioning 14 days at 70°C / 62% r.h. , Z direction)	1200	MPa	ISO 527 -2 (23°C)
Tensile Modulus (Conditioning 14 days at 70°C / 62% r.h. , Z direction)	300	MPa	ISO 527 -2 (80°C)
Tensile Elongation at Break (Conditioning 14 days at 70°C / 62% r.h. , Z direction)	34	%	ISO 527 -2 (23°C)
Tensile Elongation at Break (Conditioning 14 days at 70°C / 62% r.h. , Z direction)	120	%	ISO 527 -2 (80°C)
Flexural Modulus (Conditioning 14 days at 70°C / 62% r.h. , Z direction)	1300	MPa	DIN EN ISO 178
Charpy Impact Strength (notched,Conditioning 14 days at 70°C / 62% r.h. , Z direction)	11	kJ/m²	ISO 179 -1
Charpy Impact Strength (unnotched,Conditioning 14 days at 70°C / 62% r.h. , Z direction)	75	kJ/m²	ISO 179 -1
Izod Impact Strength (notched,Conditioning 14 days at 70°C / 62% r.h. , Z direction)	9.9	J/m	ISO 180
Izod Impact Strength (unnotched,Conditioning 14 days at 70°C / 62% r.h. , Z direction)	63	J/m	ISO 180

	Value	Units	Test Method / Conditions
Bulk Density	540	kg/m³	DIN EN ISO 60
Printed Part Density	1030	kg/m³	DIN EN ISO 118 3-1
Mean Particle Size	40-50	d50/μm	Laser Di_x001f_raction
Melting Temperature	203	°C	ISO 11357 ( 10 K/min)
Crystallization Temperature	165	°C	ISO 11357 ( 10 K/min)
Melt Volume Flow Rate	18	cm³/10min	ISO 1133 (2 20 °C, 2.16 kg)

	Value	Units	Test Method / Conditions
HDT/A (1.8 M Pa)	62	°C	ISO 75 -2
HDT/B (0.45 MPa)	177	°C	ISO 75 -2
Vicat/A (10 N)	192	°C	ISO 306
Vicat/B (50 N)	175	°C	ISO 306

Regulatory & Compliance

Certifications: ISO 9001:2015

AS 9100:2016

Controlled Goods Program

Solaxis Nylon 11 - PA 11 - Polyamide 11

Knowde Enhanced TDS