Solaxis Nylon 6 FR - PA 6 flame retardant - Prototyping

Identification & Functionality

Additives Included: Flame Retardant
Chemical Family: Polyamides
Polymer Name: Polyamide 6 (PA 6)
Technologies: Plastics
Product Families: Plastics — 3D Printing Polymers
Other 3D Printing Polymers

Features & Benefits

Materials Features: Chemical Resistant,
Excellent Mechanical Strength,
Good Thermal Stability,
High Fatigue Resistance,
High Strength

Applications & Uses

Markets: Automotive & Transportation,
Industrial
Applications: Automotive & Transportation — Automotive
Other Automotive Applications
Industrial — Chemical & Industrial Manufacturing
Tooling & Moldmaking
Automotive & Transportation — Transportation
Aerospace & Aviation
Plastics & Elastomers End Uses: 3D Printing Applications,
Prototyping
Plastics & Elastomers Processing Methods: 3D Printing,
Selective Laser Sintering

Properties

Color: Black
Mechanical Properties
Typical Properties
Electrical Properties
Aerospace Properties

	Value	Units	Test Method / Conditions
Tensile Strength (Drying 14 days at 80°C / vacuum,X direction)	56	MPa	ISO 527-2
Tensile Modulus (Drying 14 days at 80°C / vacuum,X direction)	4750	MPa	ISO 527 -2
Tensile Elongation at Break (Drying 14 days at 80°C / vacuum,X direction)	1.4	%	ISO 527 -2
Flexural Modulus (Drying 14 days at 80°C / vacuum,X direction)	4400	MPa	DIN EN ISO 178
Charpy Impact Strength (notched,Drying 14 days at 80°C / vacuum,X direction)	1.3	kJ/m²	ISO 179 -1
Charpy Impact Strength (unnotched,Drying 14 days at 80°C / vacuum,X direction)	4.8	kJ/m²	ISO 179 -1
Izod Impact Strength (notched,Drying 14 days at 80°C / vacuum,X direction)	1.8	J/m	ISO 180
Izod Impact Strength (unnotched,Drying 14 days at 80°C / vacuum,X direction)	5	J/m	ISO 180
Tensile Strength (Drying 14 days at 80°C / vacuum,Z direction)	33	MPa	ISO 527-2
Tensile Modulus (Drying 14 days at 80°C / vacuum,Z direction)	4500	MPa	ISO 527 -2
Tensile Elongation at Break (Drying 14 days at 80°C / vacuum,Z direction)	0.8	%	ISO 527 -2
Flexural Modulus (Drying 14 days at 80°C / vacuum,Z direction)	3850	MPa	DIN EN ISO 178
Charpy Impact Strength (notched,Drying 14 days at 80°C / vacuum,Z direction)	1	kJ/m²	ISO 179 -1
Charpy Impact Strength (unnotched,Drying 14 days at 80°C / vacuum,Z direction)	2.5	kJ/m²	ISO 179 -1
Izod Impact Strength (notched,Drying 14 days at 80°C / vacuum,Z direction)	1.5	J/m	ISO 180
Izod Impact Strength (unnotched,Drying 14 days at 80°C / vacuum,Z direction)	3.4	J/m	ISO 180
Tensile Strength (Conditioning 14 days at 70°C / 62% r.h. , X direction)	41	MPa	ISO 527-2
Tensile Modulus (Conditioning 14 days at 70°C / 62% r.h. , X direction)	2450	MPa	ISO 527 -2
Tensile Elongation at Break (Conditioning 14 days at 70°C / 62% r.h. , X direction)	2.6	%	ISO 527 -2
Flexural Modulus (Conditioning 14 days at 70°C / 62% r.h. , X direction)	2000	MPa	DIN EN ISO 178
Charpy Impact Strength (notched,Conditioning 14 days at 70°C / 62% r.h. , X direction)	1.6	kJ/m²	ISO 179 -1
Charpy Impact Strength (unnotched,Conditioning 14 days at 70°C / 62% r.h. , X direction)	7.4	kJ/m²	ISO 179 -1
Izod Impact Strength (notched,Conditioning 14 days at 70°C / 62% r.h. , X direction)	2.1	J/m	ISO 180
Izod Impact Strength (unnotched,Conditioning 14 days at 70°C / 62% r.h. , X direction)	7	J/m	ISO 180
Tensile Strength (Conditioning 14 days at 70°C / 62% r.h. , Z direction)	27	MPa	ISO 527-2
Tensile Modulus (Conditioning 14 days at 70°C / 62% r.h. , Z direction)	2450	MPa	ISO 527 -2
Tensile Elongation at Break (Conditioning 14 days at 70°C / 62% r.h. , Z direction)	1.2	%	ISO 527 -2
Flexural Modulus (Conditioning 14 days at 70°C / 62% r.h. , Z direction)	2050	MPa	DIN EN ISO 178
Charpy Impact Strength (notched,Conditioning 14 days at 70°C / 62% r.h. , Z direction)	1.1	kJ/m²	ISO 179 -1
Charpy Impact Strength (unnotched,Conditioning 14 days at 70°C / 62% r.h. , Z direction)	3.6	kJ/m²	ISO 179 -1
Izod Impact Strength (notched,Conditioning 14 days at 70°C / 62% r.h. , Z direction)	1.5	J/m	ISO 180
Izod Impact Strength (unnotched,Conditioning 14 days at 70°C / 62% r.h. , Z direction)	3.8	J/m	ISO 180

	Value	Units	Test Method / Conditions
Bulk Density	550	kg/m³	DIN EN ISO 60
Printed Part Density	1300	kg/m³	DIN EN ISO 118 3-1
Mean Particle Size	65-75	—	Laser Di_x001e_raction
Melting Temperature	218	°C	ISO 11357 (20 K/min)
Crystallization Temperature	169	°C	ISO 11357 (20 K/min)
Melt Volume Flow Rate	10	cm³/10min	ISO 1133 (240 °C, 2.16kg)
HDT/A (1.8 M Pa)	113	°C	ISO 75 -2
HDT/B (0.45 MPa)	207	°C	ISO 75 -2
Vicat/A (10 N)	214	°C	ISO 306
Vicat/B (50 N)	197	°C	ISO 306
Melting Behavior	Pass	—	ECE -R 118 App. 7

	Value	Units	Test Method / Conditions
UL Flammability	V-2 (0.8 -3 mm)	—	UL 94V
Hot-Wire Ignition (HWI)	PLC -4 (1 mm), PLC -3 (2 -3 mm)	—	UL 746A
Glow Wire Flammability Index (GWFI)	750	°C	DIN EN 60695 -2-12
Glow Wire Ignition Temperature (GWIT)	775	°C	DIN EN 60695 -2-13

	Value	Units	Test Method / Conditions
Flammability (12s Vertical)	Pass	—	FAR 25.853 (a)
Flammability (60s Vertical)	Pass	—	FAR 25.853 (a)
Gas Toxicity	Pass	—	BSS 7239 Rev A
Smoke Density (Flaming mode)	Pass	—	BSS 7238 Rev C
Smoke Density (Non-flaming mode)	Pass	—	BSS 7238 Rev C

Regulatory & Compliance

Certifications: ISO 9001:2015

AS 9100:2016

Controlled Goods Program

Solaxis Nylon 6 FR - PA 6 flame retardant

Knowde Enhanced TDS