Products

Tasnee LD 4025N is an Additive Free Low Density Polyethylene with Melt Flow Rate of 4.0 g/10min (190°C/2.16kg). It has a suitable molecular structure to produce film with excellent mechanical properties. Tasnee LD 4025N can be easily processed on all types of extruders designed for polyethylene. The melt temperature is suggested to be in the range of 150 – 190°C. Excellent properties of the film are achieved with a blow-up ratio of 2.5:1 and recommended film thickness range from 15 to 40 μm.

Tasnee LD 4025AS is a Low Density Polyethylene with a Melt Flow Rate of 4.0 g/10min (190°C/2.16kg), recommended for mono and multilayer thin gage blown film extrusion. Tasnee LD 4025AS contains slip and anti- blocking additives and has a suitable molecular structure to produce film with excellent mechanical and optical properties. Tasnee LD 4025AS can be easily processed on all types of extruders designed for polyethylene. The melt temperature is suggested to be in the range of 150 – 190°C. Excellent properties of the film are achieved with a blow - up ratio of 2.5:1 and recommended film thickness range from 15 to 40 μm.

Tasnee LD 0725N is a Low Density Polyethylene with a Melt Flow Rate of 0.75 g/10min (190°C/2.16kg), recommended for mono and multilayer blown film extrusion. Tasnee LD 0725N is an additive free grade and has a suitable molecular structure to make film with excellent mechanical and optical properties. Tasnee LD 0725N can be easily processed on all types of extruders designed for polyethylene. The melt temperature is suggested to be in the range of 170 – 220°C. Excellent properties of the film are achieved with a blow-up ratio of 2:1 and recommended film thickness range from 25 to 100 μm.

Tasnee LD 1925AS is a Low Density Polyethylene with a Melt Flow Rate of 1.9 g/10min (190°C/2.16kg), recommended for mono and multilayer blown film extrusion. Tasnee LD 1925AS contains slip and anti- blocking additives and has a suitable molecular structure to produce film with excellent mechanical and optical properties. Tasnee LD 1925AS can be easily processed on all types of extruders designed for polyethylene. The melt temperature is suggested to be in the range of 160 – 190°C. Excellent properties of the film are achieved with a blow - up ratio of 2:1 and recommended film thickness range from 25 to 60 μm.

Tasnee PP H3080 is a Polypropylene Homopolymer with a Melt Flow Rate (MFR) of 8 g/10min. Tasnee PP H3080 is designed for cast polypropylene (CPP) film, both for metallization and general purpose applications with excellent processability characteristics. Cast film produced by Tasnee PP H3080 offers excellent transparency, gloss and high stiffness.

Tasnee PP H1045 is a Polypropylene Homopolymer with a Melt Flow Rate (MFR) of 4.5 g/10min. Tasnee PP H1045 is designed for high extrusion speed lines to make stretch tapes, offering low water-carry-over and low shrinkage. Good balance of strength, shrinkage, splitting tendency. It is compliant to food contact regulations.

Tasnee PP H1030 is a Polypropylene Homopolymer with a Melt Flow Rate (MFR) of 3 g/10min. Tasnee PP H1030 is designed for stretch tape from water bath and chill roll, offering low water-carry-over and low shrinkage. Its good mechanical properties and compliance to food contact regulations allow it to be used in various applications.

Tasnee PP H3030 is a Polypropylene Homopolymer with a Melt Flow Rate (MFR) of 3.0 g/10min. Tasnee PP H3030 is designed for Bi-axial Oriented Polypropylene (BOPP) film applications, offering excellent transparency and gloss, high stiffness and excellent processability. Tasnee PP H3030 is formulated to be used for both general purpose and metallized films.

Tasnee PP H3030T is a Polypropylene Homopolymer with a Melt Flow Rate (MFR) of 3.0 g/10min. Tasnee PP H3030T is designed for Bi-axial Oriented Polypropylene (BOPP) film applications, offering excellent transparency and gloss, high stiffness and excellent processability. Tasnee PP H3030T is designed for High Speed Bi-axial Oriented Polypropylene (BOPP) film lines. Tasnee PP H3030T is formulated to be used for both general purpose and metallized films.