Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Technologies
- Product Families
Features & Benefits
- Materials Features
- Main Characteristics
- Availability of qualities conforming to the FDA standard.
- Optimum qualities of mechanical resistance, hardness and rigidity.
- Excellent sliding and friction qualities.
- High strength
- Electrically insulating
- Resistant to many greases, oils and fuels
- High toughness
- Good slide and wear resistance
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Industry Applications
- Heavy duty industry
- Conveyor technology
- Textile industry
- Engine manufacturing
- Mechanical engineering
Properties
- Flame Rating
- Mechanical Properties
- Thermal Properties
- Typical Properties
- Electrical Properties
- Miscellaneous Properties
| Value | Units | Test Method / Conditions | |
| Modulus of Elasticity (1 mm/min) | 3500.0 | MPa | DIN EN ISO 527-2 |
| Tensile strength (50 mm/min) | 83.0 | MPa | DIN EN ISO 527-2 |
| Tensile Strength at Yield (50 mm/min) | 80.0 | MPa | DIN EN ISO 527-2 |
| Elongation At Yield (50 mm/min) | 4.0 | % | DIN EN ISO 527-2 |
| Elongation at Break (50 mm/min) | 55.0 | % | DIN EN ISO 527-2 |
| Flexural Strength (2 mm/min , 10 N) | 109.0 | MPa | DIN EN ISO 178 |
| Modulus Of Elasticity (Flex Test, 2 mm/min , 10 N) | 3200.0 | MPa | DIN EN ISO 178 |
| Compression Strength (1%. 5 mm/min , 10 N) | 19.0 | MPa | EN ISO 604 |
| Compression Strength (2%. 5 mm/min , 10 N) | 36.0 | MPa | EN ISO 604 |
| Compression Modulus (5 mm/min , 10 N) | 2900.0 | MPa | EN ISO 604 |
| Impact Strength (Charpy, max. 7.5j) | No break | Kj/m² | DIN EN ISO 179-1EU |
| Notched Impact Strength (Charpy, max. 7.5j) | 4.0 | Kj/m² | DIN EN ISO 179-1EU |
| Ball Indentation Hardness | 170.0 | MPa | ISO 2039-1 |
| Value | Units | Test Method / Conditions | |
| Glass Transition Temperature | 40.0 | ºC | DIN 53765 |
| Melting Temperature | 215.0 | ºC | DIN 53765 |
| Service Temperature (Short term) | 170.0 | ºC | — |
| Service Temperature (Long term) | 100.0 | ºC | — |
| Thermal Expansion (23 - 60 ºC long) | 12.0 | 10⁻⁵ K⁻¹ | DIN EN ISO 11359-1;2 |
| Thermal Expansion (23 - 100ºC long) | 12.0 | 10⁻⁵ K⁻¹ | DIN EN ISO 11359-1;2 |
| Specific Heat | 1.7 | J/(g+K) | ISO 22007-4:2008 |
| Thermal Conductivity | 0.38 | W/(K+m) | ISO 22007-4:2008 |
| Value | Units | Test Method / Conditions | |
| Density | 1.15 | g/cm³ | — |
| Value | Units | Test Method / Conditions | |
| Surface Resistance | 10¹⁴ | Ω | DIN IEC 60093 |
| Value | Units | Test Method / Conditions | |
| Water Absorption (24h, 23ºC) | 0.2 | % | DIN EN ISO 62 |
| Water Absorption (96h, 23ºC) | 0.4 | % | DIN EN ISO 62 |
| Resistance To Hot Mater / Bases | (+) | — | — |
| Flammability (UL94) | HB | — | DIN IEC 60995-11-10 |
Regulatory & Compliance
Packaging & Availability
- Availability
We manufacture bars, tubes and plates In addition to natural polyamide , we manufacture different grades of polyamides, whether loaded with molybdenum bisulfide , graphite carbon , oil, polyethylene , etc.