Properties
- Mechanical Properties
- Thermal Properties
- Typical Properties
- Electrical Properties
| Value | Units | Test Method / Conditions | |
| Tensile Modulus (Dry) | 17500 | Mpa | ISO 527-1 527-2 |
| Charpy Impact Strength (Dry-as-Mold Condition) | 80 | kg/m² | ISO 179-1 |
| Tensile Modulus (Condition) | 10800 | Mpa | ISO 527-1 527-2 |
| Tensile Strain at Break (Dry) | 2.6 | % | ISO 527-1 527-2 |
| Charpy Notched Impact Strength (Dry-as-Mold Condition) | 19 | kg/m² | ISO 179-1 |
| Tensile Strain at Break (Condition) | 4.4 | - | - |
| Charpy Impact Strength (Conditioned to Equilibirium at 23°C, 50%RH) | 93 | kg/m² | ISO 179-1 |
| Charpy Impact Strength (Conditioned) | 93 | kg/m² | ISO 179-1 |
| Charpy Impact Strength (Dry) | 80 | kg/m² | ISO 179-1 |
| Charpy Notched Impact Strength (Conditioned to Equilibirium at 23°C, 50%RH) | 26 | kg/m² | ISO 179-1 |
| Flexural Modulus (Dry-as-Mold Condition) | 16800 | Mpa | ISO 178 |
| Charpy Notched Impact Strength (Conditioned) | 26 | kg/m² | ISO 179-1 |
| Flexural Strength (Dry-as-Mold Condition) | 380 | Mpa | ISO 178 |
| Charpy Notched Impact Strength (Dry) | 19 | kg/m² | ISO 179-1 |
| Flexural Modulus (Conditioned to Equilibirium at 23°C, 50%RH) | 10300 | Mpa | ISO 178 |
| Flexural Modulus (Conditioned) | 10300 | Mpa | ISO 178 |
| Tensile Modulus (Dry-as-Mold Condition) | 17500 | Mpa | ISO 527-1 527-2 |
| Flexural Modulus (Dry) | 16800 | Mpa | ISO 178 |
| Flexural Strength (Conditioned to Equilibirium at 23°C, 50%RH) | 265 | Mpa | ISO 178 |
| Tensile Strain at Break (Dry-as-Mold Condition) | 2.6 | % | ISO 527-1 527-2 |
| Flexural Strength (Conditioned) | 265 | Mpa | ISO 178 |
| Tensile Stress at Break (Dry-as-Mold Condition) | 240 | Mpa | ISO 527-1 527-2 |
| Flexural Strength (Dry) | 380 | Mpa | ISO 178 |
| Tensile Modulus (Conditioned to Equilibirium at 23°C, 50%RH) | 10800 | Mpa | ISO 527-1 527-2 |
| Tensile Strain at Break (Conditioned to Equilibirium at 23°C, 50%RH) | 4.4 | % | ISO 527-1 527-2 |
| Tensile Strain at Break (Conditioned) | 4.4 | % | ISO 527-1 527-2 |
| Tensile Stress at Break (Conditioned to Equilibirium at 23°C, 50%RH) | 170 | Mpa | ISO 527-1 527-2 |
| Tensile Stress at Break (Conditioned) | 170 | Mpa | ISO 527-1 527-2 |
| Tensile Stress at Break (Dry) | 240 | Mpa | ISO 527-1 527-2 |
| Value | Units | Test Method / Conditions | |
| Coefficient of Linear Thermal Expansion | 2.2 | 10⁻⁵/°C | ISO 11359-2 |
| Deflection Temperature (Under load 0.45MPa) | 218 | °C | ISO 75-2 |
| Deflection Temperature (Under load 1.8MPa) | 214 | °C | ISO 75-1 |
| Value | Units | Test Method / Conditions | |
| Mold Shrinkage (Thickness : 3.2mm, Flow) | 0.1 | % | - |
| Mold Shrinkage (Thickness : 3.2mm, Transverse) | 0.3 | % | - |
| Water Absorption (23°C in Water 24H) | 0.7 | % | ISO 62 |
| Water Absorption (23°C, 50% RH Equilibirium) | 1.1 | % | ISO 62 |
| Density | 1.7 | g/cm³ | ISO 1183 |
| Value | Units | Test Method / Conditions | |
| Electric Strength (Thickness:1mm, Dry) | 42 | MV/m | IEC 60243-1 |
| Volume Resistivity (Conditioned to Equilibirium at 23°C, 50%RH) | 2 x 10¹³ | Ω-m | IEC 60093 |
| Volume Resistivity (Dry) | 2 x 10¹³ | Ω-m | IEC 60093 |
| Electric Strength (Thickness:1mm) | 42 | MV/m | IEC 60243-1 |