Value | Units | Test Method / Conditions | |
Tensile Modulus (Dry) | 10800 | Mpa | ISO 527-1 527-2 |
Charpy Impact Strength (Dry-as-Mold Condition) | 22 | kg/m² | ISO 179-1 |
Tensile Modulus (Condition) | 7000 | MPa | ASTM D638 |
Tensile Strain at Break (Dry) | 2 | % | ISO 527-1 527-2 |
Charpy Notched Impact Strength (Dry-as-Mold Condition) | 9 | kg/m² | ISO 179-1 |
Tensile Strain at Break (Condition) | 2.5 | — | — |
Charpy Impact Strength (Conditioned to Equilibirium at 23°C, 50%RH) | 31 | kg/m² | ISO 179-1 |
Charpy Impact Strength (Conditioned) | 31 | kg/m² | ISO 179-1 |
Charpy Impact Strength (Dry) | 22 | kg/m² | ISO 179-1 |
Charpy Notched Impact Strength (Conditioned to Equilibirium at 23°C, 50%RH) | 14 | kg/m² | ISO 179-1 |
Charpy Notched Impact Strength (Conditioned) | 14 | kg/m² | ISO 179-1 |
Charpy Notched Impact Strength (Dry) | 9 | kg/m² | ISO 179-1 |
Flexural Modulus (Conditioned to Equilibirium at 23°C, 50%RH) | 6000 | Mpa | ISO 178 |
Flexural Modulus (Dry-as-Mold Condition) | 9200 | Mpa | ISO 178 |
Flexural Modulus (Conditioned) | 6000 | Mpa | ISO 178 |
Flexural Strength (Dry-as-Mold Condition) | 250 | Mpa | ISO 178 |
Flexural Modulus (Dry) | 9200 | Mpa | ISO 178 |
Flexural Strength (Conditioned to Equilibirium at 23°C, 50%RH) | 140 | Mpa | ISO 178 |
Flexural Strength (Conditioned) | 140 | Mpa | ISO 178 |
Rockwell Hardness (Dry-as-Mold Condition) | 118 | R Scale | ISO 2039 |
Flexural Strength (Dry) | 250 | Mpa | ISO 178 |
Rockwell Hardness (Conditioned to Equilibirium at 23°C, 50%RH) | 102 | R Scale | ISO 2039 |
Tensile Modulus (Dry-as-Mold Condition) | 10800 | Mpa | ISO 527-1 527-2 |
Rockwell Hardness (R Scale, Condtioned) | 102 | kg/m² | ISO 2039 |
Tensile Strain at Break (Dry-as-Mold Condition) | 2 | % | ISO 527-1 527-2 |
Rockwell Hardness (R Scale, Dry) | 118 | kg/m² | ISO 2039 |
Tensile Stress at Break (Dry-as-Mold Condition) | 148 | Mpa | ISO 527-1 527-2 |
Tensile Modulus (Conditioned to Equilibirium at 23°C, 50%RH) | 7000 | Mpa | ISO 527-1 527-2 |
Tensile Strain at Break (Conditioned to Equilibirium at 23°C, 50%RH) | 2.5 | % | ISO 527-1 527-2 |
Tensile Strain at Break (Conditioned) | 2.5 | % | ISO 527-1 527-2 |
Tensile Stress at Break (Conditioned to Equilibirium at 23°C, 50%RH) | 110 | Mpa | ISO 527-1 527-2 |
Tensile Stress at Break (Conditioned) | 110 | Mpa | ISO 527-1 527-2 |
Tensile Stress at Break (Dry) | 148 | Mpa | ISO 527-1 527-2 |
Tensile Stress at Break (Condition) | 110 | Mpa | ISO 527-1 527-2 |
Value | Units | Test Method / Conditions | |
Coefficient of Linear Thermal Expansion (Dry-as-Mold Condition) | 3 | 10⁻⁵/°C | ISO 11359-2 |
Deflection Temperature (Under load 0.45MPa) | 215 | °C | ISO 75-2 |
Deflection Temperature (Under load 1.8MPa) | 200 | °C | ISO 75-1 |
Coefficient of Linear Thermal Expansion | 3 | 10⁻⁵/°C | ISO 11359-2 |
Coefficient of Linear Thermal Expansion (Conditioned to Equilibirium at 23°C, 50%RH) | 3 | 10⁻⁵/°C | ISO 11359-2 |
Value | Units | Test Method / Conditions | |
Mold Shrinkage (Thickness : 3.2mm, Flow) | 0.7 | % | — |
Mold Shrinkage (Thickness : 3.2mm, Transverse) | 0.8-1.0 | % | — |
Mold Shrinkage (Thickness : 3.2mm, Transverse) | 0.8 - 1.0 | % | — |
Water Absorption (23°C in Water 24H) | 1 | % | ISO 62 |
Water Absorption (23°C, 50% RH Equilibirium) | 0.2 | % | ISO 62 |
Density | 1.64 | g/cm³ | ISO 1183 |
Flammability (mmt V-0) | 0.87 | — | UL-94 |
Value | Units | Test Method / Conditions | |
Dielectric Constant (106Hz) | 3.8 | — | IEC 60250 |
Dissipation Factor (106Hz) | 0.02 | — | IEC 60250 |
Dielectric Constant | 3.8 | 10⁶ Hz | IEC 60250 |
Dissipation Factor | 0.02 | 10⁶ Hz | IEC 60250 |
Electric Strength (Thickness:1mm) | 25 | MV/m | IEC 60243-1 |