Properties
- Mechanical Properties
- Thermal Properties
- Typical Properties
- Electrical Properties
| Value | Units | Test Method / Conditions | |
| Tensile Modulus (Dry) | 2500 | Mpa | ISO 527-1 527-2 |
| Charpy Notched Impact Strength (Dry-as-Mold Condition) | 5 | kg/m² | ISO 179-1 |
| Tensile Modulus (Condition) | 900 | Mpa | ISO 527-1 527-2 |
| Tensile Strain at Break (Dry) | 68 | % | ISO 527-1 527-2 |
| Tensile Strain at Break (Condition) | min. 200 | — | — |
| Tensile strain at yield (Dry) | 4 | % | ISO 527-1 527-2 |
| Tensile Strain at Yield (Condition) | 24 | % | ISO 527-1 527-2 |
| Flexural Modulus (Dry-as-Mold Condition) | 2500 | Mpa | ISO 178 |
| Flexural Strength (Dry-as-Mold Condition) | 97 | Mpa | ISO 178 |
| Charpy Notched Impact Strength (Conditioned to Equilibirium at 23°C, 50%RH) | 43 | kg/m² | ISO 179-1 |
| Charpy Notched Impact Strength (Conditioned) | 43 | kg/m² | ISO 179-1 |
| Rockwell Hardness (Dry-as-Mold Condition) | 112 | R Scale | ISO 2039 |
| Charpy Notched Impact Strength (Dry) | 5 | kg/m² | ISO 179-1 |
| Flexural Modulus (Conditioned to Equilibirium at 23°C, 50%RH) | 900 | Mpa | ISO 178 |
| Tensile Modulus (Dry-as-Mold Condition) | 2500 | Mpa | ISO 527-1 527-2 |
| Flexural Modulus (Conditioned) | 900 | Mpa | ISO 178 |
| Tensile Strain at Break (Dry-as-Mold Condition) | 68 | % | ISO 527-1 527-2 |
| Flexural Modulus (Dry) | 2500 | Mpa | ISO 178 |
| Flexural Strength (Conditioned to Equilibirium at 23°C, 50%RH) | 33 | Mpa | ISO 178 |
| Tensile Strain at Yield (Dry-as-Mold Condition) | 4 | % | ISO 527-1 527-2 |
| Flexural Strength (Conditioned) | 33 | Mpa | ISO 178 |
| Tensile Stress at Yield (Dry-as-Mold Condition) | 78 | Mpa | ISO 527-1 527-2 |
| Flexural Strength (Dry) | 97 | Mpa | ISO 178 |
| Rockwell Hardness (Conditioned to Equilibirium at 23°C, 50%RH) | 90 | R Scale | ISO 2039 |
| Rockwell Hardness (R Scale, Condtioned) | 90 | kg/m² | ISO 2039 |
| Rockwell Hardness (R Scale, Dry) | 112 | kg/m² | ISO 2039 |
| Tensile Modulus (Conditioned to Equilibirium at 23°C, 50%RH) | 900 | Mpa | ISO 527-1 527-2 |
| Tensile Strain at Break (Conditioned to Equilibirium at 23°C, 50%RH) | min. 200 | % | ISO 527-1 527-2 |
| Tensile Strain at Break (Conditioned) | min. 200 | % | ISO 527-1 527-2 |
| Tensile Strain at Yield (Conditioned to Equilibirium at 23°C, 50%RH) | 24 | % | ISO 527-1 527-2 |
| Tensile Strain at Yield (Conditioned) | 24 | % | ISO 527-1 527-2 |
| Tensile Strain at Yield (Dry) | 4 | % | ISO 527-1 527-2 |
| Tensile Stress at Yield (Conditioned to Equilibirium at 23°C, 50%RH) | 40 | Mpa | ISO 527-1 527-2 |
| Tensile Stress at yield (Conditioned) | 40 | Mpa | ISO 527-1 527-2 |
| Tensile Stress at yield (Dry) | 78 | Mpa | ISO 527-1 527-2 |
| Value | Units | Test Method / Conditions | |
| Coefficient of Linear Thermal Expansion (Dry-as-Mold Condition) | 9.6 | 10⁻⁵/°C | ISO 11359-2 |
| Deflection Temperature (Under load 0.45MPa) | 154 | °C | ISO 75-2 |
| Deflection Temperature (Under load 1.8MPa) | 56 | °C | ISO 75-1 |
| Coefficient of Linear Thermal Expansion | 9.6 | 10⁻⁵/°C | ISO 11359-2 |
| Coefficient of Linear Thermal Expansion (Conditioned to Equilibirium at 23°C, 50%RH) | 9.6 | 10⁻⁵/°C | ISO 11359-2 |
| Value | Units | Test Method / Conditions | |
| Mold Shrinkage (Thickness : 3.2mm, Flow) | 1 | % | — |
| Mold Shrinkage (Thickness : 3.2mm, Transverse) | 1.3 | % | — |
| Water Absorption (23°C in Water 24H) | 1.8 | % | ISO 62 |
| Water Absorption (23°C, 50% RH Equilibirium) | 2.8 | % | ISO 62 |
| Density | 1.13 | g/cm³ | ISO 1183 |
| Value | Units | Test Method / Conditions | |
| Comparative Tracking Index (Conditioned to Equilibirium at 23°C, 50%RH) | min. 600 | — | IEC 60112 |
| Dielectric Constant (106Hz, Conditioned) | 3.7 | — | IEC 60250 |
| Dielectric Constant (106Hz, Dry) | 3.4 | — | IEC 60250 |
| Comparative Tracking Index (Dry-as-Mold Condition) | min. 600 | — | IEC 60112 |
| Dielectric Constant (Conditioned to Equilibirium at 23°C, 50%RH) | 3.7 | 10⁶ Hz | IEC 60250 |
| Dissipation Factor (106Hz, Conditioned) | 0.08 | — | IEC 60250 |
| Dissipation Factor (106Hz, Dry) | 0.02 | — | IEC 60250 |
| Dissipation Factor (Conditioned to Equilibirium at 23°C, 50%RH) | 0.08 | 10⁶ Hz | IEC 60250 |
| Dielectric Constant (Dry-as-Mold Condition) | 3.4 | 10⁶ Hz | IEC 60250 |
| Electric Strength (Thickness:1mm, Conditioned to Equilibirium at 23°C, 50%RH) | 37/33 | MV/m | IEC 60243-1 |
| Dissipation Factor (Dry-as-Mold Condition) | 0.02 | 10⁶ Hz | IEC 60250 |
| Electric Strength (Thickness:1mm, Conditioned) | 33 | MV/m | IEC 60243-1 |
| Electric Strength (Thickness:1mm, Dry-as-Mold Condition) | 37/33 | MV/m | IEC 60243-1 |
| Electric Strength (Thickness:1mm, Dry) | 37 | MV/m | IEC 60243-1 |
| Volume Resistivity (Conditioned to Equilibirium at 23°C, 50%RH) | 3 x 10¹³ | Ω-m | IEC 60093 |
| Volume Resistivity (Conditioned) | 8 x 10¹¹ | Ω-m | IEC 60093 |
| Volume Resistivity (Dry) | 3 x 10¹³ | Ω-m | IEC 60093 |
| Volume Resistivity (Dry-as-Mold Condition) | 8 x 10¹¹ | Ω-m | IEC 60093 |
| Comparative tracking Index | min. 600 | — | IEC 60112 |