Properties
- Flame Rating
- Mechanical Properties
- Thermal Properties
- Typical Properties
- Electrical Properties
Value | Units | Test Method / Conditions | |
Tensile Modulus (Dry) | 2900 | Mpa | ISO 527-1 527-2 |
Charpy Notched Impact Strength (Dry-as-Mold Condition) | 4 | kg/m² | ISO 179-1 |
Tensile Modulus (Condition) | 1200 | Mpa | ISO 527-1 527-2 |
Tensile Strain at Break (Dry) | 30 | % | ISO 527-1 527-2 |
Tensile Strain at Break (Condition) | 150 | - | - |
Tensile strain at yield (Dry) | 4 | % | ISO 527-1 527-2 |
Tensile Strain at Yield (Condition) | 22 | % | ISO 527-1 527-2 |
Flexural Modulus (Dry-as-Mold Condition) | 2800 | Mpa | ISO 178 |
Flexural Strength (Dry-as-Mold Condition) | 105 | Mpa | ISO 178 |
Charpy Notched Impact Strength (Conditioned to Equilibirium at 23°C, 50%RH) | 31 | kg/m² | ISO 179-1 |
Charpy Notched Impact Strength (Conditioned) | 31 | kg/m² | ISO 179-1 |
Charpy Notched Impact Strength (Dry) | 4 | kg/m² | ISO 179-1 |
Rockwell Hardness (Dry-as-Mold Condition) | 120 | R Scale | ISO 2039 |
Flexural Modulus (Conditioned to Equilibirium at 23°C, 50%RH) | 1200 | Mpa | ISO 178 |
Flexural Modulus (Conditioned) | 1200 | Mpa | ISO 178 |
Tensile Modulus (Dry-as-Mold Condition) | 2900 | Mpa | ISO 527-1 527-2 |
Flexural Modulus (Dry) | 2800 | Mpa | ISO 178 |
Tensile Strain at Break (Dry-as-Mold Condition) | 30 | % | ISO 527-1 527-2 |
Flexural Strength (Conditioned to Equilibirium at 23°C, 50%RH) | 49 | Mpa | ISO 178 |
Flexural Strength (Conditioned) | 49 | Mpa | ISO 178 |
Tensile Strain at Yield (Dry-as-Mold Condition) | 4 | % | ISO 527-1 527-2 |
Flexural Strength (Dry) | 105 | Mpa | ISO 178 |
Tensile Stress at Yield (Dry-as-Mold Condition) | 82 | Mpa | ISO 527-1 527-2 |
Rockwell Hardness (Conditioned to Equilibirium at 23°C, 50%RH) | 85 | R Scale | ISO 2039 |
Rockwell Hardness (R Scale, Condtioned) | 85 | kg/m² | ISO 2039 |
Rockwell Hardness (R Scale, Dry) | 120 | kg/m² | ISO 2039 |
Tensile Modulus (Conditioned to Equilibirium at 23°C, 50%RH) | 1200 | Mpa | ISO 527-1 527-2 |
Tensile Strain at Break (Conditioned to Equilibirium at 23°C, 50%RH) | 150 | % | ISO 527-1 527-2 |
Tensile Strain at Break (Conditioned) | 150 | % | ISO 527-1 527-2 |
Tensile Strain at Yield (Conditioned to Equilibirium at 23°C, 50%RH) | 22 | % | ISO 527-1 527-2 |
Tensile Strain at Yield (Conditioned) | 22 | % | ISO 527-1 527-2 |
Tensile Strain at Yield (Dry) | 4 | % | ISO 527-1 527-2 |
Tensile Stress at Yield (Conditioned to Equilibirium at 23°C, 50%RH) | 55 | Mpa | ISO 527-1 527-2 |
Tensile Stress at yield (Conditioned) | 55 | Mpa | ISO 527-1 527-2 |
Tensile Stress at yield (Dry) | 82 | Mpa | ISO 527-1 527-2 |
Value | Units | Test Method / Conditions | |
Coefficient of Linear Thermal Expansion (Dry-as-Mold Condition) | 9.6 | 10⁻⁵/°C | ISO 11359-2 |
Deflection Temperature (Under load 0.45MPa) | 170 | °C | ISO 75-2 |
Deflection Temperature (Under load 1.8MPa) | 61 | °C | ISO 75-1 |
Coefficient of Linear Thermal Expansion | 9.6 | 10⁻⁵/°C | ISO 11359-2 |
Coefficient of Linear Thermal Expansion (Conditioned to Equilibirium at 23°C, 50%RH) | 9.6 | 10⁻⁵/°C | ISO 11359-2 |
Value | Units | Test Method / Conditions | |
Mold Shrinkage (Thickness : 3.2mm, Flow) | 0.9 | % | - |
Mold Shrinkage (Thickness : 3.2mm, Transverse) | 1.1 | % | - |
Water Absorption (23°C in Water 24H) | 1.8 | % | ISO 62 |
Water Absorption (23°C, 50% RH Equilibirium) | 2.8 | % | ISO 62 |
Density | 1.14 | g/cm³ | ISO 1183 |
Flammability (mmt V-2) | 0.84 | - | UL-94 |
Value | Units | Test Method / Conditions | |
Comparative Tracking Index (Conditioned to Equilibirium at 23°C, 50%RH) | min. 600 | - | IEC 60112 |
Dielectric Constant (106Hz, Conditioned) | 3.7 | - | IEC 60250 |
Dielectric Constant (106Hz, Dry) | 3.4 | - | IEC 60250 |
Comparative Tracking Index (Dry-as-Mold Condition) | min. 600 | - | IEC 60112 |
Dielectric Constant (Conditioned to Equilibirium at 23°C, 50%RH) | 3.7 | 10⁶ Hz | IEC 60250 |
Dissipation Factor (106Hz, Conditioned) | 0.08 | - | IEC 60250 |
Dissipation Factor (106Hz, Dry) | 0.02 | - | IEC 60250 |
Dissipation Factor (Conditioned to Equilibirium at 23°C, 50%RH) | 0.08 | 10⁶ Hz | IEC 60250 |
Dielectric Constant (Dry-as-Mold Condition) | 3.4 | 10⁶ Hz | IEC 60250 |
Electric Strength (Thickness:1mm, Conditioned to Equilibirium at 23°C, 50%RH) | 33 | MV/m | IEC 60243-1 |
Dissipation Factor (Dry-as-Mold Condition) | 0.02 | 10⁶ Hz | IEC 60250 |
Electric Strength (Thickness:1mm, Conditioned) | 33 | MV/m | IEC 60243-1 |
Electric Strength (Thickness:1mm, Dry-as-Mold Condition) | 37 | MV/m | IEC 60243-1 |
Electric Strength (Thickness:1mm, Dry) | 37 | MV/m | IEC 60243-1 |
Volume Resistivity (Conditioned to Equilibirium at 23°C, 50%RH) | 8 x 10¹¹ | Ω-m | IEC 60093 |
Volume Resistivity (Conditioned) | 8 x 10¹¹ | Ω-m | IEC 60093 |
Volume Resistivity (Dry) | 3 x 10¹³ | Ω-m | IEC 60093 |
Volume Resistivity (Dry-as-Mold Condition) | 3 x 10¹³ | Ω-m | IEC 60093 |
Comparative tracking Index | min. 600 | - | IEC 60112 |