Value | Units | Test Method / Conditions | |
Tensile Modulus (Dry) | 2700 | Mpa | ISO 527-1 527-2 |
Charpy Impact Strength (Dry-as-Mold Condition) | 82 | kg/m² | ISO 179-1 |
Tensile Modulus (Condition) | 840 | Mpa | ISO 527-1 527-2 |
Tensile Strain at Break (Dry) | 15 | % | ISO 527-1 527-2 |
Charpy Notched Impact Strength (Dry-as-Mold Condition) | 3 | kg/m² | ISO 179-1 |
Tensile Strain at Break (Condition) | 28 | - | - |
Tensile Strain at Yield (Dry) | 4 | % | ISO 527-1 527-2 |
Charpy Impact Strength (Conditioned to Equilibirium at 23°C, 50%RH) | 120 | kg/m² | ISO 179-1 |
Charpy Impact Strength (Conditioned) | 120 | kg/m² | ISO 179-1 |
Flexural Modulus (Dry-as-Mold Condition) | 2500 | Mpa | ISO 178 |
Charpy Impact Strength (Dry) | 82 | kg/m² | ISO 179-1 |
Charpy Notched Impact Strength (Conditioned to Equilibirium at 23°C, 50%RH) | 12 | kg/m² | ISO 179-1 |
Flexural Strength (Dry-as-Mold Condition) | 90 | Mpa | ISO 178 |
Charpy Notched Impact Strength (Conditioned) | 12 | kg/m² | ISO 179-1 |
Charpy Notched Impact Strength (Dry) | 3 | kg/m² | ISO 179-1 |
Rockwell Hardness (Dry-as-Mold Condition) | 116 | R Scale | ISO 2039 |
Flexural Modulus (Conditioned to Equilibirium at 23°C, 50%RH) | 800 | Mpa | ISO 178 |
Flexural Modulus (Conditioned) | 800 | Mpa | ISO 178 |
Tensile Modulus (Dry-as-Mold Condition) | 2700 | Mpa | ISO 527-1 527-2 |
Flexural Modulus (Dry) | 2500 | Mpa | ISO 178 |
Flexural Strength (Conditioned to Equilibirium at 23°C, 50%RH) | 30 | Mpa | ISO 178 |
Tensile Strain at Break (Dry-as-Mold Condition) | 15 | % | ISO 527-1 527-2 |
Flexural Strength (Conditioned) | 30 | Mpa | ISO 178 |
Tensile Strain at Yield (Dry-as-Mold Condition) | 4 | % | ISO 527-1 527-2 |
Flexural Strength (Dry) | 90 | Mpa | ISO 178 |
Tensile Stress at Yield (Dry-as-Mold Condition) | 68 | Mpa | ISO 527-1 527-2 |
Rockwell Hardness (Conditioned to Equilibirium at 23°C, 50%RH) | 95 | R Scale | ISO 2039 |
Rockwell Hardness (R Scale, Condtioned) | 95 | kg/m² | ISO 2039 |
Rockwell Hardness (R Scale, Dry) | 116 | kg/m² | ISO 2039 |
Tensile Modulus (Conditioned to Equilibirium at 23°C, 50%RH) | 840 | Mpa | ISO 527-1 527-2 |
Tensile Strain at Break (Conditioned to Equilibirium at 23°C, 50%RH) | 28 | % | ISO 527-1 527-2 |
Tensile Strain at Break (Conditioned) | 28 | % | ISO 527-1 527-2 |
Tensile Stress at Yield (Conditioned to Equilibirium at 23°C, 50%RH) | 42 | Mpa | ISO 527-1 527-2 |
Tensile Stress at yield (Conditioned) | 42 | Mpa | ISO 527-1 527-2 |
Tensile Stress at yield (Dry) | 68 | Mpa | ISO 527-1 527-2 |
Value | Units | Test Method / Conditions | |
Coefficient of Linear Thermal Expansion | 8 | 10⁻⁵/°C | ISO 11359-2 |
Deflection Temperature (Under load 0.45MPa) | 120 | °C | ISO 75-2 |
Deflection Temperature (Under load 1.8MPa) | 53 | °C | ISO 75-1 |
Value | Units | Test Method / Conditions | |
Mold Shrinkage (Thickness : 3.2mm, Flow) | 1.5 | % | - |
Mold Shrinkage (Thickness : 3.2mm, Transverse) | 1.8 | % | - |
Water Absorption (23°C in Water 24H) | 1.6 | % | ISO 62 |
Water Absorption (23°C, 50% RH Equilibirium) | 2.5 | % | ISO 62 |
Density | 1.18 | g/cm³ | ISO 1183 |
Value | Units | Test Method / Conditions | |
Dielectric Constant (106Hz, Dry) | 3.4 | - | IEC 60250 |
Dissipation Factor (106Hz, Conditioned) | 0.02 | - | IEC 60250 |
Volume Resistivity (Conditioned to Equilibirium at 23°C, 50%RH) | 7 x 10¹² | Ω-m | IEC 60093 |
Volume Resistivity (Conditioned) | 7 x 10¹² | Ω-m | IEC 60093 |
Volume Resistivity (Dry) | 3 x 10¹³ | Ω-m | IEC 60093 |
Dielectric Constant | 3.4 | 10⁶ Hz | IEC 60250 |
Dissipation Factor | 0.02 | 10⁶ Hz | IEC 60250 |
Volume Resistivity (Dry-as-Mold Condition) | 3 x 10¹³ | Ω-m | IEC 60093 |