Properties
- Mechanical Properties
- Thermal Properties
- Typical Properties
- Electrical Properties
| Value | Units | Test Method / Conditions | |
| Tensile Modulus (Dry) | 6400 | Mpa | ISO 527-1 527-2 |
| Charpy Impact Strength (Dry-as-Mold Condition) | 41 | kg/m² | ISO 179-1 |
| Tensile Modulus (Condition) | 3200 | Mpa | ISO 527-1 527-2 |
| Tensile Strain at Break (Dry) | 2.9 | % | ISO 527-1 527-2 |
| Charpy Notched Impact Strength (Dry-as-Mold Condition) | 3 | kg/m² | ISO 179-1 |
| Tensile Strain at Break (Condition) | 3.8 | — | — |
| Charpy Impact Strength (Conditioned to Equilibirium at 23°C, 50%RH) | 48 | kg/m² | ISO 179-1 |
| Charpy Impact Strength (Conditioned) | 48 | kg/m² | ISO 179-1 |
| Charpy Impact Strength (Dry) | 41 | kg/m² | ISO 179-1 |
| Flexural Modulus (Dry-as-Mold Condition) | 6300 | Mpa | ISO 178 |
| Charpy Notched Impact Strength (Conditioned to Equilibirium at 23°C, 50%RH) | 6 | kg/m² | ISO 179-1 |
| Charpy Notched Impact Strength (Conditioned) | 6 | kg/m² | ISO 179-1 |
| Flexural Strength (Dry-as-Mold Condition) | 118 | Mpa | ISO 178 |
| Charpy Notched Impact Strength (Dry) | 3 | kg/m² | ISO 179-1 |
| Flexural Modulus (Conditioned to Equilibirium at 23°C, 50%RH) | 3300 | Mpa | ISO 178 |
| Flexural Modulus (Conditioned) | 3300 | Mpa | ISO 178 |
| Rockwell Hardness (Dry-as-Mold Condition) | 119 | R Scale | ISO 2039 |
| Flexural Modulus (Dry) | 6300 | Mpa | ISO 178 |
| Tensile Modulus (Dry-as-Mold Condition) | 6400 | Mpa | ISO 527-1 527-2 |
| Flexural Strength (Conditioned to Equilibirium at 23°C, 50%RH) | 70 | Mpa | ISO 178 |
| Flexural Strength (Conditioned) | 70 | Mpa | ISO 178 |
| Tensile Strain at Break (Dry-as-Mold Condition) | 2.9 | % | ISO 527-1 527-2 |
| Flexural Strength (Dry) | 118 | Mpa | ISO 178 |
| Tensile Stress at Break (Dry-as-Mold Condition) | 70 | Mpa | ISO 527-1 527-2 |
| Rockwell Hardness (Conditioned to Equilibirium at 23°C, 50%RH) | 103 | R Scale | ISO 2039 |
| Rockwell Hardness (R Scale, Condtioned) | 103 | kg/m² | ISO 2039 |
| Rockwell Hardness (R Scale, Dry) | 119 | kg/m² | ISO 2039 |
| Tensile Modulus (Conditioned to Equilibirium at 23°C, 50%RH) | 3200 | Mpa | ISO 527-1 527-2 |
| Tensile Strain at Break (Conditioned to Equilibirium at 23°C, 50%RH) | 3.8 | % | ISO 527-1 527-2 |
| Tensile Strain at Break (Conditioned) | 3.8 | % | ISO 527-1 527-2 |
| Tensile Stress at Break (Conditioned to Equilibirium at 23°C, 50%RH) | 50 | Mpa | ISO 527-1 527-2 |
| Tensile Stress at Break (Conditioned) | 50 | Mpa | ISO 527-1 527-2 |
| Tensile Stress at Break (Dry) | 70 | Mpa | ISO 527-1 527-2 |
| Value | Units | Test Method / Conditions | |
| Coefficient of Linear Thermal Expansion (Dry-as-Mold Condition) | 5 | 10⁻⁵/°C | ISO 11359-2 |
| Deflection Temperature (Under load 0.45MPa) | 196 | °C | ISO 75-2 |
| Deflection Temperature (Under load 1.8MPa) | 130 | °C | ISO 75-1 |
| Coefficient of Linear Thermal Expansion | 5 | 10⁻⁵/°C | ISO 11359-2 |
| Coefficient of Linear Thermal Expansion (Conditioned to Equilibirium at 23°C, 50%RH) | 5 | 10⁻⁵/°C | ISO 11359-2 |
| Value | Units | Test Method / Conditions | |
| Mold Shrinkage (Thickness : 3.2mm, Flow) | 0.4 | % | — |
| Mold Shrinkage (Thickness : 3.2mm, Transverse) | 0.8 | % | — |
| Water Absorption (23°C in Water 24H) | 1.2 | % | ISO 62 |
| Water Absorption (23°C, 50% RH Equilibirium) | 1.8 | % | ISO 62 |
| Density | 1.4 | g/cm³ | ISO 1183 |
| Flammability (mmt HB) | 0.81 | — | UL-94 |
| Value | Units | Test Method / Conditions | |
| Dielectric Constant (106Hz) | 3.6 | — | IEC 60250 |
| Dissipation Factor (106Hz) | 0.02 | — | IEC 60250 |
| Electric Strength (Thickness:1mm) | 42 | MV/m | IEC 60243-1 |
| Volume Resistivity (Conditioned to Equilibirium at 23°C, 50%RH) | 5 x 10¹¹ | Ω-m | IEC 60093 |
| Volume Resistivity (Conditioned) | 5 x 10¹¹ | Ω-m | IEC 60093 |
| Dielectric Constant (Dry-as-Mold Condition) | 3.6 | 10⁶ Hz | IEC 60250 |
| Volume Resistivity (Dry) | 2 x 10¹³ | Ω-m | IEC 60093 |
| Dissipation Factor (Dry-as-Mold Condition) | 0.02 | 10⁶ Hz | IEC 60250 |
| Electric Strength (Thickness:1mm, Dry-as-Mold Condition) | 42 | MV/m | IEC 60243-1 |
| Volume Resistivity (Dry-as-Mold Condition) | 2 x 10¹³ | Ω-m | IEC 60093 |