Vectorply E-LT 1200-P

Identification & Functionality

Chemical Family

Glass Beads & Fibers

Reinforcement Form

0/90 Fabric

Reinforcement Material

Glass Fibers

Composite Materials Functions

Reinforcement

Architecture

0/90

Technologies

Composite Materials

Product Families

Composite Materials — Reinforcements

Glass Fiber

Features & Benefits

Materials Features

Corrosion Resistant,

Cost Effective,

High Impact Resistance,

Light Weight

Applications & Uses

Markets

Automotive & Transportation,

Building & Construction,

Consumer Goods,

Industrial

Applications

Building & Construction — Building Materials

Pipes & Plumbing

Industrial — Chemical & Industrial Manufacturing

Other Industrial Applications

Building & Construction — Infrastructure, Roads & Paving

Pavement, Highways, Roads & Bridges

Industrial — Military & Defense

Advanced Materials,

Body Armor

Industrial — Power, Water & Utilities

Renewable Energy

Consumer Goods — Sports & Recreation

Automotive & Transportation — Transportation

Aerospace & Aviation,

Marine

Compatible Polymers & Resins

Polyesters,

Vinyl Esters

Composites End Use

Pipe Reinforcement,

Snowboards

Properties

Physical Form

Fabric

Dry Thickness

0.017 (0.43)

Total Weight

11.94 (405)

Roll Width

50 (1270)

Roll Weight

204 (93)

Roll Length

186 (170)

Technical Details & Test Data

Fiber Architecture Data

• 0 ° : 5.97 oz/sq.yd / 202 g/sq.m
• 45 ° : n/a
• 90 ° : 5.97 oz/sq.yd / 202 g/sq.m
• -45 ° : n/a
• Chopped Mat : n/a

Laminated Properties

Laminate Weight

	E-LT 1200-P Resin Infused	E-LT 1200-P Open Mold
Fiber Resin Total	0.40 kg/sq.m 0.17 kg/sq.m 0.58 kg/sq.m	0.40 kg/sq.m 0.33 kg/sq.m 0.74 kg/sq.m

Physical Properties

	E-LT 1200-P Resin Infused	E-LT 1200-P Open Mold
Density Fiber Content Thickness	1.90 g/cc 52% by Vol. 0.3 mm	1.69 g/cc 37% by Vol. 0.4 mm

Laminate Modulii

	E-LT 1200-P Resin Infused	E-LT 1200-P Open Mold
Ex Ey Gxy Ex,flex. Ey,flex.	26.95 GPa 26.95 GPa 4.53 GPa 25.60 GPa 25.60 GPa	19.46 GPa 19.46 GPa 3.24 GPa 18.48 GPa 18.48 GPa

Ultimate Stress

	E-LT 1200-P Resin Infused	E-LT 1200-P Open Mold
Long. Ten. Long. Comp. Trans. Ten. Trans. Comp. In-Plane Shear Long. Flex. Trans. Flex.	510.2 MPa 510.2 MPa 510.2 MPa 510.2 MPa 90.6 MPa 609.0 MPa 609.0 MPa	368.4 MPa 368.4 MPa 368.4 MPa 368.4 MPa 64.7 MPa 439.7 MPa 439.7 MPa

In-Plane Stiffness, "EA" 

	E-LT 1200-P Resin Infused	E-LT 1200-P Open Mold
(EA)x (EA)y (GA)xy	8,197 N/mm 8,197 N/mm 1,378 N/mm	8,475 N/mm 8,475 N/mm 1,410 N/mm

Ultimate In-Plane Load

	E-LT 1200-P Resin Infused	E-LT 1200-P Open Mold
Long. Ten. Long. Comp. Trans. Ten. Trans. Comp. In-Plane Shear	155 N/mm 155 N/mm 155 N/mm 155 N/mm 28 N/mm	160 N/mm 160 N/mm 160 N/mm 160 N/mm 28 N/mm

Packaging & Availability

Packaging Type

Bags,

Boxes