Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Reinforcement Form
- Reinforcement Material
- Composite Materials Functions
- Architecture
- 0/90
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Applications
- Compatible Polymers & Resins
- Composites End Use
Properties
- Physical Form
- Dry Thickness
- 0.032 (0.81)
- Total Weight
- 31.32 (1062)
- Roll Width
- 50 (1270)
- Roll Weight
- 220 (100)
- Roll Length
- 80 (73)
Technical Details & Test Data
- Fiber Architecture Data
- 0 ° : 27.96 oz/sq.yd / 948 g/sq.m
- 45 ° : n/a
- 90 ° : 3.36 oz/sq.yd / 114 g/sq.m
- -45 ° : n/a
- Duraspun : n/a
- Laminated Properties
Laminate Weight
E-LT 2900
Resin InfusedE-LT 2900
Open MoldFiber
Resin
Total1.06 kg/sq.m
0.46 kg/sq.m
1.52 kg/sq.m1.06 kg/sq.m
0.87 kg/sq.m
1.93 kg/sq.mPhysical Properties
E-LT 2900
Resin InfusedE-LT 2900
Open MoldDensity
Fiber Content
Thickness1.90 g/cc
52% by Vol.
0.8 mm1.69 g/cc
37% by Vol.
1.1 mmLaminate Modulii
E-LT 2900
Resin InfusedE-LT 2900
Open MoldEx
Ey
Gxy
Ex,flex.
Ey,flex.36.71 GPa
17.07 GPa
4.53 GPa
34.87 GPa
16.22 GPa26.79 GPa
12.01 GPa
3.24 GPa
25.45 GPa
11.41 GPaUltimate Stress
E-LT 2900
Resin InfusedE-LT 2900
Open MoldLong. Ten.
Long. Comp.
Trans. Ten.
Trans. Comp.
In-Plane Shear
Long. Flex.
Trans. Flex.694.9 MPa
694.9 MPa
323.2 MPa
323.2 MPa
90.6 MPa
829.5 MPa
385.7 MPa507.2 MPa
507.2 MPa
227.4 MPa
227.4 MPa
64.8 MPa
605.4 MPa
271.4 MPaIn-Plane Stiffness, "EA"
E-LT 2900
Resin InfusedE-LT 2900
Open Mold(EA)x
(EA)y
(GA)xy29,274 N/mm
13,613 N/mm
3,614 N/mm30,604 N/mm
13,722 N/mm
3,699 N/mmUltimate In-Plane Load
E-LT 2900
Resin InfusedE-LT 2900
Open MoldLong. Ten.
Long. Comp.
Trans. Ten.
Trans. Comp.
In-Plane Shear554 N/mm
554 N/mm
258 N/mm
258 N/mm
72 N/mm579 N/mm
579 N/mm
260 N/mm
260 N/mm
74 N/mm