Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Reinforcement Form
- Reinforcement Material
- Composite Materials Functions
- Architecture
- 0/90
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Applications
- Compatible Polymers & Resins
- Composites End Use
Properties
- Physical Form
- Dry Thickness
- 0.033 (0.84)
- Total Weight
- 31.36 (1063)
- Roll Width
- 50 (1270)
- Roll Weight
- 189 (86)
- Roll Length
- 68 (62)
Technical Details & Test Data
- Fiber Architecture Data
- 0 ° : 17.92 oz/sq.yd / 608 g/sq.m
- 45 ° : n/a
- 90 ° : 13.44 oz/sq.yd / 456 g/sq.m
- -45 ° : n/a
- Chopped Mat : n/a
- Laminated Properties
Laminate Weight
E-LT 3200
Resin InfusedE-LT 3200
Open MoldFiber
Resin
Total1.06 kg/sq.m
0.46 kg/sq.m
1.52 kg/sq.m1.06 kg/sq.m
0.87 kg/sq.m
1.93 kg/sq.mPhysical Properties
E-LT 3200
Resin InfusedE-LT 3200
Open MoldDensity
Fiber Content
Thickness1.90 g/cc
52% by Vol.
0.8 mm1.69 g/cc
37% by Vol.
1.1 mmLaminate Modulii
E-LT 3200
Resin InfusedE-LT 3200
Open MoldEx
Ey
Gxy
Ex,flex.
Ey,flex.28.75 GPa
25.17 GPa
4.53 GPa
27.31 GPa
23.91 GPa20.81 GPa
18.11 GPa
3.24 GPa
19.77 GPa
17.20 GPaUltimate Stress
E-LT 3200
Resin InfusedE-LT 3200
Open MoldLong. Ten.
Long. Comp.
Trans. Ten.
Trans. Comp.
In-Plane Shear
Long. Flex.
Trans. Flex.544.2 MPa
544.2 MPa
476.5 MPa
476.5 MPa
90.6 MPa
649.6 MPa
568.7 MPa393.9 MPa
393.9 MPa
342.9 MPa
342.9 MPa
64.8 MPa
470.2 MPa
409.2 MPaIn-Plane Stiffness, "EA"
E-LT 3200
Resin InfusedE-LT 3200
Open Mold(EA)x
(EA)y
(GA)xy22,956 N/mm
20,096 N/mm
3,619 N/mm23,798 N/mm
20,715 N/mm
3,703 N/mmUltimate In-Plane Load
E-LT 3200
Resin InfusedE-LT 3200
Open MoldLong. Ten.
Long. Comp.
Trans. Ten.
Trans. Comp.
In-Plane Shear435 N/mm
435 N/mm
380 N/mm
380 N/mm
72 N/mm451 N/mm
451 N/mm
392 N/mm
392 N/mm
74 N/mm