Vectorply E-QX 1900

Identification & Functionality

Chemical Family

Glass Beads & Fibers

Reinforcement Form

Multiaxial Fabric

Reinforcement Material

Glass Fibers

Composite Materials Functions

Reinforcement

Architecture

0/45/90/-45 Quadraxial

Technologies

Composite Materials

Product Families

Composite Materials — Reinforcements

Glass Fiber

Features & Benefits

Materials Features

Corrosion Resistant,

Cost Effective,

High Impact Resistance,

Light Weight

Applications & Uses

Markets

Automotive & Transportation,

Building & Construction,

Consumer Goods,

Industrial

Applications

Building & Construction — Building Materials

Pipes & Plumbing

Industrial — Chemical & Industrial Manufacturing

Other Industrial Applications

Building & Construction — Infrastructure, Roads & Paving

Pavement, Highways, Roads & Bridges

Industrial — Military & Defense

Advanced Materials,

Body Armor

Industrial — Power, Water & Utilities

Renewable Energy

Consumer Goods — Sports & Recreation

Automotive & Transportation — Transportation

Aerospace & Aviation,

Marine

Compatible Polymers & Resins

Polyesters,

Vinyl Esters

Composites End Use

Pipe Reinforcement,

Snowboards

Properties

Physical Form

Fabric

Dry Thickness

0.027 (0.69)

Total Weight

20.68 (701)

Roll Width

50 (1270)

Roll Weight

223 (101)

Roll Length

120 (110)

Technical Details & Test Data

Fiber Architecture Data

• 0 ° : 12.80 oz/sq.yd / 434 g/sq.m
• 45 ° : 3.14 oz/sq.yd / 106 g/sq.m
• 90 ° : 1.60 oz/sq.yd / 54 g/sq.m
• -45 ° : 3.14 oz/sq.yd / 106 g/sq.m
• Chopped Mat : n/a

Laminated Properties

Laminate Weight

	E-QX 1900 Resin Infused	E-QX 1900 Open Mold
Fiber Resin Total	0.70 kg/sq.m 0.33 kg/sq.m 1.03 kg/sq.m	0.70 kg/sq.m 0.57 kg/sq.m 1.27 kg/sq.m

Physical Properties

	E-QX 1900 Resin Infused	E-QX 1900 Open Mold
Density Fiber Content Thickness	1.87 g/cc 50% by Vol. 0.6 mm	1.69 g/cc 37% by Vol. 0.8 mm

Laminate Modulii

	E-QX 1900 Resin Infused	E-QX 1900 Open Mold
Ex Ey Gxy Ex,flex. Ey,flex.	28.98 GPa 16.38 GPa 6.46 GPa 27.53 GPa 15.56 GPa	21.99 GPa 12.21 GPa 4.86 GPa 20.89 GPa 11.60 GPa

Ultimate Stress

	E-QX 1900 Resin Infused	E-QX 1900 Open Mold
Long. Ten. Long. Comp. Trans. Ten. Trans. Comp. In-Plane Shear Long. Flex. Trans. Flex.	548.7 MPa 548.7 MPa 310.1 MPa 310.1 MPa 122.3 MPa 654.9 MPa 370.1 MPa	416.4 MPa 416.4 MPa 231.1 MPa 231.1 MPa 92.1 MPa 497.0 MPa 275.9 MPa

In-Plane Stiffness, "EA" 

	E-QX 1900 Resin Infused	E-QX 1900 Open Mold
(EA)x (EA)y (GA)xy	15,971 N/mm 9,026 N/mm 3,561 N/mm	16,588 N/mm 9,208 N/mm 3,669 N/mm

Ultimate In-Plane Load

	E-QX 1900 Resin Infused	E-QX 1900 Open Mold
Long. Ten. Long. Comp. Trans. Ten. Trans. Comp. In-Plane Shear	302 N/mm 302 N/mm 171 N/mm 171 N/mm 67 N/mm	314 N/mm 314 N/mm 174 N/mm 174 N/mm 69 N/mm