Vectorply E-T 0900

Identification & Functionality

Chemical Family

Glass Beads & Fibers

Reinforcement Form

Unidirectional Fabric

Reinforcement Material

Glass Fibers

Composite Materials Functions

Reinforcement

Architecture

90 Weft Unidirectional

Technologies

Composite Materials

Product Families

Composite Materials — Reinforcements

Glass Fiber

Features & Benefits

Materials Features

Corrosion Resistant,

Cost Effective,

High Impact Resistance,

Light Weight

Applications & Uses

Markets

Automotive & Transportation,

Building & Construction,

Consumer Goods,

Industrial

Applications

Building & Construction — Building Materials

Pipes & Plumbing

Industrial — Chemical & Industrial Manufacturing

Other Industrial Applications

Building & Construction — Infrastructure, Roads & Paving

Pavement, Highways, Roads & Bridges

Industrial — Military & Defense

Advanced Materials,

Body Armor

Industrial — Power, Water & Utilities

Renewable Energy

Consumer Goods — Sports & Recreation

Automotive & Transportation — Transportation

Aerospace & Aviation,

Marine

Compatible Polymers & Resins

Polyesters,

Vinyl Esters

Composites End Use

Pipe Reinforcement,

Snowboards

Properties

Physical Form

Fabric

Dry Thickness

0.014 (0.36)

Total Weight

8.96 (304)

Roll Width

50 (1270)

Roll Weight

230 (105)

Roll Length

278 (254)

Technical Details & Test Data

Fiber Architecture Data

• 0 ° : n/a
• 45 ° : n/a
• 90 ° : 8.96 oz/sq.yd / 304 g/sq.m
• -45 ° : n/a
• Chopped Mat : n/a

Laminated Properties

Laminate Weight

	E-T 0900 Resin Infused	E-T 0900 Open Mold
Fiber Resin Total	0.30 kg/sq.m 0.13 kg/sq.m 0.43 kg/sq.m	0.30 kg/sq.m 0.25 kg/sq.m 0.55 kg/sq.m

Physical Properties

	E-T 0900 Resin Infused	E-T 0900 Open Mold
Density Fiber Content Thickness	1.90 g/cc 52% by Vol. 0.2 mm	1.69 g/cc 37% by Vol. 0.3 mm

Laminate Modulii

	E-T 0900 Resin Infused	E-T 0900 Open Mold
Ex Ey Gxy Ex,flex. Ey,flex.	14.35 GPa 39.29 GPa 4.53 GPa 13.63 GPa 37.32 GPa	9.97 GPa 28.73 GPa 3.24 GPa 9.47 GPa 27.29 GPa

Ultimate Stress

	E-T 0900 Resin Infused	E-T 0900 Open Mold
Long. Ten. Long. Comp. Trans. Ten. Trans. Comp. In-Plane Shear Long. Flex. Trans. Flex.	143.5 MPa 143.5 MPa 743.8 MPa 743.8 MPa 90.6 MPa 136.3 MPa 887.8 MPa	99.7 MPa 99.7 MPa 543.8 MPa 543.8 MPa 64.7 MPa 94.7 MPa 649.1 MPa

In-Plane Stiffness, "EA" 

	E-T 0900 Resin Infused	E-T 0900 Open Mold
(EA)x (EA)y (GA)xy	3,276 N/mm 8,968 N/mm 1,034 N/mm	3,258 N/mm 9,392 N/mm 1,058 N/mm

Ultimate In-Plane Load

	E-T 0900 Resin Infused	E-T 0900 Open Mold
Long. Ten. Long. Comp. Trans. Ten. Trans. Comp. In-Plane Shear	33 N/mm 33 N/mm 170 N/mm 170 N/mm 21 N/mm	33 N/mm 33 N/mm 178 N/mm 178 N/mm 21 N/mm

Packaging & Availability

Packaging Type

Bags,

Boxes