Properties
- Physical Form
- Dry Thickness
- 0.031 (0.79)
- Total Weight
- 15.49 (525)
- Roll Width
- 50 (1270)
- Roll Weight
- 187 (85)
- Roll Length
- 138 (126)
Technical Details & Test Data
- Fiber Architecture Data
- 0 ° : n/a
- 45 ° : n/a
- 90 ° : 15.49 oz/sq.yd / 525 g/sq.m
- -45 ° : n/a
- Chopped Mat : n/a
- Laminated Properties
Laminate Weight
E-T 1600
Resin InfusedE-T 1600
Open MoldFiber
Resin
Total0.53 kg/sq.m
0.23 kg/sq.m
0.75 kg/sq.m0.53 kg/sq.m
0.43 kg/sq.m
0.96 kg/sq.mPhysical Properties
E-T 1600
Resin InfusedE-T 1600
Open MoldDensity
Fiber Content
Thickness1.90 g/cc
52% by Vol.
0.4 mm1.69 g/cc
37% by Vol.
0.6 mmLaminate Modulii
E-T 1600
Resin InfusedE-T 1600
Open MoldEx
Ey
Gxy
Ex,flex.
Ey,flex.14.35 GPa
39.30 GPa
4.53 GPa
13.64 GPa
37.33 GPa9.97 GPa
28.73 GPa
3.24 GPa
9.47 GPa
27.30 GPaUltimate Stress
E-T 1600
Resin InfusedE-T 1600
Open MoldLong. Ten.
Long. Comp.
Trans. Ten.
Trans. Comp.
In-Plane Shear
Long. Flex.
Trans. Flex.143.5 MPa
143.5 MPa
744.0 MPa
744.0 MPa
90.6 MPa
136.4 MPa
888.0 MPa99.7 MPa
99.7 MPa
544.0 MPa
544.0 MPa
64.7 MPa
94.7 MPa
649.3 MPaIn-Plane Stiffness, "EA"
E-T 1600
Resin InfusedE-T 1600
Open Mold(EA)x
(EA)y
(GA)xy5,663 N/mm
15,504 N/mm
1,788 N/mm5,632 N/mm
16,236 N/mm
1,829 N/mmUltimate In-Plane Load
E-T 1600
Resin InfusedE-T 1600
Open MoldLong. Ten.
Long. Comp.
Trans. Ten.
Trans. Comp.
In-Plane Shear57 N/mm
57 N/mm
294 N/mm
294 N/mm
36 N/mm56 N/mm
56 N/mm
307 N/mm
307 N/mm
37 N/mm