Aegis® H95C1ZP

Identification & Functionality

Chemical Family

Polyamides

Polymer Name

Polyamide 6/66 (PA 6/66)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Features & Benefits

Labeling Claims

Food Contact Acceptable

Materials Features

Chemical Resistant,

Food Contact Acceptable,

Good Abrasion Resistance,

Good Toughness,

Heat Resistance,

Medium Viscosity,

Moderate Strength,

Odorless

Applications & Uses

Markets

Printing & Packaging

Applications

Printing & Packaging — Packaging

Food & Beverage Packaging

Plastics & Elastomers End Uses

Cast Films,

Film,

Food Packaging,

Form Fill Seal Packaging,

Retort Pouches

Plastics & Elastomers Processing Methods

Blown Film Extrusion,

Cast Film Extrusion,

Extrusion,

Film Extrusion

Properties

Color

Translucent,

White

Physical Form

Pellets,

Solid

Thermal Properties

	Value	Units	Test Method / Conditions
Melting Point	194 (381)	°C (°F)	ASTM D-3418

Test Parameter

	Value	Units	Test Method / Conditions
Extractable Content	Max. 0.8	%	SOP-702-307
Viscosity, FAV	95	—	ASTM D-789
Melt Flow Rate (at 235°C, 1.0 kg)	3.5	g/10 min	ASTM D-1238
SAV (at 96% Sulfuric Acid)	3.31	—	—
Specific Gravity (at 23°C)	1.13	—	ASTM D-792

Mechanical Properties (Film)

	Value	Units	Test Method / Conditions
Elongation (at 23°C, 50% RH) - MD*	700	%	ASTM D-882
Elongation (at 23°C, 50% RH) - TD*	660	%	ASTM D-882
Puncture Energy	1.4	Joules	ASTM D-5748
Puncture Force	57	Newtons	ASTM D-5748
Puncture Penetration to Break	50	mm	ASTM D-5748
Tensile Modulus (at 23°C, 50%RH) - MD*	285	MPa	ASTM D-882
Tensile Modulus (at 23°C, 50%RH) - TD*	220	MPa	ASTM D-882
Tensile Strength (at 23°C, 50% RH) - MD*	100	MPa	ASTM D-882
Tensile Strength (at 23°C, 50% RH) - TD*	80	MPa	ASTM D-882
Tensile Yield (at 23°C, 50%RH) - MD*	24	MPa	ASTM D-882
Tensile Yield (at 23°C, 50%RH) - TD*	19	MPa	ASTM D-882

Gas Barrier Properties

	Value	Units	Test Method / Conditions
Oxygen Permeability (at 23°C, 0% RH)	43	cc-mil/m²/day	ASTM D-3958
Water Vapor Permeability (at 38°C, 100% RH)	830	gm-mil/m²/day	ASTM F-1249

Moisture Properties

	Value	Units	Test Method / Conditions
Moisture Content	Max. 0.08	%	ASTM D-6869
Moisture Content (at 24 hours)	1.6	%	ASTM D-570
Moisture Content (at 50% RH)	3.1	%	ASTM D-570
Moisture Content (at Saturation)	10.5	%	ASTM D-570

Note

* MD = Machine Direction and TD = Traverse Direction. Test specimens were obtained from 2-mil thick cast film and tested as conditioned (23°C,50%RH).

Regulatory & Compliance

Certifications & Compliance

Canadian Environmental Protection Act (CEPA),

FDA 21 CFR 177.1500,

FDA Compliant

Chemical Inventories

AICS (Australia),

ENCS (Japan),

IECSC (China),

KECI (Korea),

NZIoC (New Zealand),

TSCA (USA)

Regulatory Information

• Aegis® H95C1ZP copolymer conforms to FDA requirements of 21 CFR 177.1500 (a) (4) and (b) (4.2) for use as articles or components of articles intended for use in processing, handling, and packaging food, provided that the finished articles meet the applicable use and/or extraction limitations and requirements of relevant regulations.
• Aegis® H95C1ZP is also suitable for use as a component of food packaging according to the European Plastic Regulations (EC) No. 10/2011, amended in 2018 to No. 2018/79.

Technical Details & Test Data

Extrusion Guidelines

1. Melt Viscosity vs. Temperature
   Melt Temperature: 194°C (381°F)
   Two key factors affect the melt viscosity (stiffness or fluidity of the melt) :
   1. The molecular weight (MW) of the resin: Higher MW resins will have a higher melt viscosity than lower MW resins.
   2. Temperature of the melt for any given MW resin: Higher process temperatures will provide a more fluid melt viscosity than lower process temperatures.
       
2. Typical Barrel Profile for Cast Films
   Barrel : 230-260°C (446-500°F)
   Adapter : 260-266°C (500-510°F)
   Die : 260°C (500°F)
   Process Melt Temperature : 240-260°C (464-500°F)
    
3. Typical Barrel Profile for Tubular (Blown) Films
   Barrel : 246-254°C (474-490°F)
   Adapter : 260°C (500°F)
   Die : 254°C (490°F)
   Process Melt Temperature : 240-260°C (464-500°F)
    
4. Screw Parameters
   Metering Section : 40%
   Transition Section : 3 to 4 flights
   Feed Section : Balance of screw length
   Compression Ratio : 3.5:1 to 4.0:1
   L/D Ratio : 24:1
    
5. Metering Section Flight Depth
   

   Screw Diameter	Recommended Depth
   1"	0.055"
   1.5"	0.060"
   2"	0.070"
   2.5"	0.080"
   3.5"	0.100"
   4.5"	0.115"
   6"	0.135"

Packaging & Availability

Packaging Type

Totes (IBC)

Storage & Handling

Storage Information

Store in original container. Keep containers tightly closed in a dry, cool and well-ventilated place.

Material Handling

Aegis® H95C1ZP copolymer is supplied in sealed containers and drying prior to processing is not required. However, higher moisture is the primary cause of processing issues. If drying becomes necessary, a dehumidifying or desiccant dryer operating at 80°C (176°F) is recommended. Drying time is dependent on moisture level. More information about safe handling procedures can be obtained by requesting the Safety Data Sheet.