Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Technologies
- Product Families
Features & Benefits
- Labeling Claims
Applications & Uses
- Markets
- Application Area
- Cure Method
- Surface Preparation
Steel surfaces are to be abrasive blasted with chloride free abrasive. Exterior applications to SSPC SP-10 Near White metal finish. Immersion applications to SSPC SP-5 White metal 3 to 5 mil profile. Grind flat all burrs, weld seams, radius sharp edges. Fresh blasted ferrous surfaces to be primed immediately to prevent oxidation of surface. For hand applications Prime with EE-121HT Prime.
Concrete surfaces should be degreased if oil and grease contamination is present. Degreased surface shall be high pressure washed, acid etched, and high pressure washed again so surface is clean and free of all grease, oils and surface laitance. Existing coatings should be abrasive blasted to clean concrete. For hand applications Prime with EE-10.
- Mixing
Thoroughly mix Activator into Base with mixing stick or drill with low speed mixing blade scraping sides and bottom of container or mixing board. Mix by Volume 3 parts Base to 1-part Activator. Or by weight 100 grams base to 31 grams activator. Mix thoroughly to produce an even colored and streak-free material.
- Application
Brush: medium to stiff bristle of sufficient quality that bristles do not pull out and stick in coating. Trim or tape to <1” nap. Roller: good quality 1/8” nap.
ARCOR Cartridge Sprayer: Heat to 165F. Piston ‘3’; Tip Air ‘4’.
Plural Spray: 0.039-0.045 tip, 3,500-4,500 PSI, Heat to 200ºF Base, 140ºF Activator. Ambient Temperature and Humidity will affect temperature and pressure setting. Consult ARCOR.
Airless Spray: Contact ARCOR.
All spray equipment should employ traps to prevent water and oil from contaminating coating and screens to prevent particulate contamination.- Application Temperature
- Keep between 55 to 95ºF(17 to 35ºC). Substrate: Keep between 45 to 105ºF(7 to 40ºC). The difference in temperature of the substrate and the material should never exceed 10ºF(5ºC). Substrate shall be a minimum of 5ºF(3ºC) above dew point. Do not apply if relative humidity exceeds 90%. If necessary heat metal prior to surface preparation using electric heater or heat lamp. Never use gas, oil or kerosene heaters as they will leave a greasy residue on metal surface. For best results keep all material in warm area overnight(75ºF+, 24ºC) for ease of mixing. If necessary base component of material can be heated by microwave for 30-45 seconds for a 1 KG Base unit or by warm water bath. Heat activator by warm water bath only. If necessary let material cool before application.
- Overcoat / Cure Time
- By brush, roller or squeegee recoat while material is still soft, but tack-free, between 1-3 hours at 77ºF(25ºC). IMPORTANT: It is highly recommended that prior to overcoat that the prior coat be fully wiped with MEK or Acetone. If overcoat window is exceeded abrade surface with course sandpaper, grinder or brush blast and wipe with MEK or Acetone. By spray application recoat between 1/2-1 hours at 77ºF(25ºC). Full cure before immersion 72 hours at 77ºF(25ºC). Add 1 hour’s additional cure time for each 10ºF(-12.2ºC) below 77ºF(25ºC). Required Force Cure with heat for best performance for 2 hours at 175ºF(121ºC)/ 300ºF(148.9ºC) for 3 hours.
- Clean Up
Clean tools immediately after use with M.E.K., Acetone, 98+% Isopropyl Alcohol or similar
Properties
- Temperature Properties
- Specifications
- Note
Coverage:1mil = 25 micron; 1 Gal = 3.785 L; 10.77ft2 = M2
- Chemical Resistance
Water Excellent Alkalis Excellent Inorganic Acids Excellent Organic Acids Excellent Organic Solvents Excellent - Film Thickness
Spray Application: 1-Coat 30 to 70 mils
Hand Application: 2-3 Coats 20-25 mils
Final DFT Specified by Need: Consult ARCOR- Film Thickness
20-70 mils(.75- 1.75 mm)/coat Exterior: min. 20 mils, Immersion: min. 30 mils
- Flexibility
Good; Very Good with Polyester or Fiberglass Mat; 1.5 oz/ft2 (.5 KG/M2)
- Mix Ratio
3:1 by Volume (Base : Activator) 100 gm: 31 gm by weight
| Value | Units | Test Method / Conditions | |
| Maximum Temperature for Immersion Service | 191.0 | °C | — |
| Temperature Spike Tolerance for Immersion Service (3hrs) | 246.0 | °C | — |
| Recommended Force Cure Temperature (2hrs) | 79.0 | °C | — |
| Recommended Force Cure Temperature (3hrs) | 149.0 | °C | — |
| Maximum Temperature for Dry Heat | 260.0 | °C | — |
| Temperature Spike Tolerance for Dry Heat | 304.0 | °C | — |
| Value | Units | Test Method / Conditions | |
| Solid Content | 100.0 | % Volume | — |
| Viscosity | 100,000-150,000 | cps | — |
| Pot Life (at 72°F) | 15.0 | min/100gr | — |
| Coverage (at 1604/mils) | 1.0 | ft² / gal / coat | — |
| Coverage (at 149/mils) | 1.0 | m²/gal | — |
| Coverage (at 3785/microns) | 1.0 | m²/gal | — |
Packaging & Availability
- Weight per Gallon
- 10.4 lbs (4.7 KG)
- 1.25kg (2.7lbs.)/Liter
Storage & Handling
- Shelf Life
- 5 Years (at 13-35ºC)