Properties
- Blown Film Properties
- Control Properties
- Note
- 1 LDPE: 25 μm thick film, obtained from a 75 mm extruder, with blow up ratio of 2:1, die gap 1 mm and Die rate 1,75 kg/h.cm (MD = Machine Direction and TD = Transversal Direction).
- 2 ND: Not Determined.
- 3 25 μm thick film, temperature: 38° C, 100% RH.
Value | Units | Test Method / Conditions | |
Tensile Strength (at Break, MD) ¹ | 25.0 | MPa | ASTM D882 |
Tensile Strength (at Break, TD) ¹ | 20.0 | MPa | ASTM D882 |
Elongation (at Break, MD) ¹ | 380.0 | % | ASTM D882 |
Elongation (at Break, TD) ¹ | 870.0 | % | ASTM D882 |
Dart Drop Impact Strength ¹ | 64.0 | g/F50 | ASTM D1709 |
Elmendorf Tear Strength (TD) ¹ | 56.0 | gF | ASTM D1922 |
Haze ¹ | 8.0 | % | ASTM D1003 |
Gloss (Angle 60°) ¹ | 76.0 | % | ASTM D2457 |
Flexural Modulus (1% Secant, MD) | 70 | MPa | D 882 |
Flexural Modulus (1% Secant, TD) | 70 | MPa | D 882 |
Value | Units | Test Method / Conditions | |
Melt Flow Rate (at 190°C, 2.16kg) | 8.3 | g/10 min | ASTM D1238 |
Density | 0.918 | g/cm³ | ASTM D1505 |