Properties
- Control Properties
- Typical Properties - Plaque Properties
- Note
- Test specimens from compression molded plaque according to ASTM D4703.
- Plaque Thickness: a) 2mm. b) 3mm c) 6mm. NB = No break.
Value | Units | Test Method / Conditions | |
Melt Flow Rate (190°C / 2.16 kg) | 0.7 | g/10 | ASTM D 1238 |
Melt Flow Rate (190°C/21.6 kg) | 50.0 | g/10 min | ASTM D 1238 |
Density | 0.962 | g/cm³ | ASTM D 792 |
Value | Units | Test Method / Conditions | |
Tensile Strength at Yield ᵃ | 32.0 | MPa | ASTM D 638 |
Tensile Strength at Break ᵃ | 22.0 | MPa | ASTM D 638 |
Flexural Modulus (1% secant) ᵇ | 1600.0 | MPa | ASTM D 2240 |
Hardness ᶜ | 64.0 | — | ASTM D 1693 |
Izod Impact Strength ᵇ | 89.0 | J/m | ASTM D 256 |
Environmental Stress Cracking Resistance (notch 0.3 mm, at 50°C, 10% Igepal CO630) ᵃ | 19.0 | h/F50 | ASTM D 1693 |
Environmental Stress Cracking Resistance (notch 0.3 mm, at 50°C, 100% Igepal CO630) ᵃ | 24.0 | h/F50 | ASTM D 1693 |
Deflection Temperature (under load, at 0.455 MPa) ᵇ | 79.0 | °C | ASTM D 648 |
Vicat Softening Temperature (at 10 N)ᵇ | 128.0 | °C | ASTM D 1525 |