Typical Properties - Plaque Properties:
- Test specimens from compression molded plaque according to ASTM D4703. Plaque Thickness: a) 2mm. b) 3mm c) 6mm. NB = No break
Value | Units | Test Method / Conditions | |
C14 Content | min. 96 | % | ASTM D 6866 |
Value | Units | Test Method / Conditions | |
Melt Flow Rate (at 190°C, 2.16kg) | 2.0 | g/10 min | ASTM D 1238 |
Density | 0.952 | g/cm³ | ASTM D 792 |
Value | Units | Test Method / Conditions | |
Tensile Strength (at Yield) ᵃ | 27.0 | MPa | ASTM D 638 |
Tensile Strength (at Break) ᵃ | 36.0 | MPa | ASTM D 638 |
Flexural Modulus (1% Secant) ᵇ | 1110.0 | MPa | ASTM D 790 |
Shore D Hardness ᶜ | 62.0 | — | ASTM D 2240 |
Izod Impact Strength ᵇ | 65.0 | J/m | ASTM D 256 |
Environmental Stress Cracking Resistance (Notch 0.3 mm, 50°C, 10% Igepal CO630) ᵃ | 35.0 | h/F50 | ASTM D 1693 |
Environmental Stress Cracking Resistance (Notch 0.3 mm, 50°C, 100% Igepal CO630) ᵃ | 65.0 | h/F50 | ASTM D 1693 |
Deflection Temperature Under Load (at 0.455 MPa) ᵇ | 65.0 | °C | ASTM D 648 |
Vicat Softening Temperature (at 10 N) ᵇ | 126.0 | °C | ASTM D 1525 |