Typical properties correspond to average values obtained in our laboratories. Test specimens prepared from compression molded sheet made according to ASTM D 4703. Thickness of test piece: a) 2 mm; b) 3 mm.
| Value | Units | Test Method / Conditions | |
| C14 Content | min. 95 | % | ASTM D 6866 |
| Value | Units | Test Method / Conditions | |
| Melt Flow Rate (at 190°C, 2.16kg) | 0.34 | g/10 min | ASTM D1238 |
| Density | 0.956 | g/cm³ | ASTM D792 |
| Value | Units | Test Method / Conditions | |
| Melt Flow Rate (at 190°C, 21.6kg) | 28.0 | g/10 min | ASTM D 1238 |
| Tensile Strength (at Yield) ᵃ | 30.0 | MPa | ASTM D 638 |
| Tensile Strength (at Break) ᵃ | 30.0 | MPa | ASTM D 638 |
| Flexural Modulus (1% Secant) ᵇ | 1250.0 | MPa | ASTM D 790 |
| Tensile Impact Strength (at 23°C) | 110.0 | kJ/m² | ISO 8256 |
| Environmental Stress Cracking Resistance (Notch 0.3 mm, 50°C, 10% Igepal CO630) ᵃ | 30.0 | h/F50 | ASTM D 1693 |
| Deflection Temperature Under Load (at 0.455 MPa) ᵇ | 70.0 | °C | ASTM D 648 |
| Vicat Softening Temperature (at 10 N) ᵇ | 127.0 | °C | ASTM D 1525 |