SLH0820/30AF

Identification & Functionality

Additives Included

Anti-Blocking Agent,

Processing Aid

Chemical Family

Polyethylenes,

Polyolefins

Polymer Name

Linear Low Density Polyethylene (LLDPE)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Basic Thermoplastics

Polyolefins

Features & Benefits

Labeling Claims

Bio-based,

Low Carbon Footprint (PCF),

Sustainable,

Sustainable Polyethylene

Materials Features

Good Mechanical Properties,

Good Processability,

Low Carbon Content,

Low Gel

Applications & Uses

Markets

Printing & Packaging

Applications

Printing & Packaging — Packaging

Industrial & Transport Packaging

Compatible Polymers & Resins

High-Density Polyethylene (HDPE),

Low-Density Polyethylene (LDPE)

Plastics & Elastomers End Uses

Bags,

Cast Films,

Industrial Sacks,

Laminates,

Sacks

Plastics & Elastomers Processing Methods

Blown Film Extrusion,

Cast Film Extrusion,

Extrusion,

Film Extrusion

Properties

Typical Properties

	Value	Units	Test Method / Conditions
C14 Content	min. 84	%	ASTM D 6866

Blown Film Properties

	Value	Units	Test Method / Conditions
Tensile Strength (at Break, MD)	40.0	MPa	ASTM D882
Tensile Strength (at Break, TD)	40.0	MPa	ASTM D882
Elongation (at Break, MD)	1190.0	%	ASTM D882
Elongation (at Break, TD)	1370.0	%	ASTM D882
Flexural Modulus (1% Secant, MD)	190.0	MPa	ASTM D882
Flexural Modulus (1% Secant, TD)	220.0	MPa	ASTM D882
Dart Drop Impact Strength	410.0	g/F50	ASTM D1709
Elmendorf Tear Strength (MD)	600.0	gF	ASTM D1922
Elmendorf Tear Strength (TD)	2020.0	gF	ASTM D1922

Control Properties

	Value	Units	Test Method / Conditions
Melt Flow Rate (at 190°C, 2.16kg)	0.8	g/10 min	ASTM D1238
Density	0.92	g/cm³	ASTM D1505

Note

Blown Film Properties:

• 100 μm Film Gage, obtained in 40 mm extruder, with 2:1 BUR. die gap 1.0 mm, (MD: Machine direction; TD: Transversal direction).