SLL318

Identification & Functionality

Additives Included

Antioxidant

Chemical Family

Polyethylenes,

Polyolefins

Polymer Name

Linear Low Density Polyethylene (LLDPE)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Basic Thermoplastics

Polyolefins

Features & Benefits

Labeling Claims

Bio-based,

Low Carbon Footprint (PCF),

Sustainable,

Sustainable Polyethylene

Materials Features

Excellent Sealability,

Good Mechanical Properties,

Low Carbon Content

Applications & Uses

Markets

Electrical & Electronics

Applications

Electrical & Electronics — Wire & Cable

Jacketing & Insulation

Compatible Polymers & Resins

High-Density Polyethylene (HDPE),

Low-Density Polyethylene (LDPE),

Polyethylene Cross-Linked (PEX)

Plastics & Elastomers End Uses

Electrical Insulation,

Film,

Liners,

Pipes,

Stretch Films

Plastics & Elastomers Processing Methods

Cast Film Extrusion,

Extrusion,

Film Extrusion

Properties

Blown Film Properties

	Value	Units	Test Method / Conditions
Tensile Strength (at Break, MD)	30.0	MPa	ASTM D882
Tensile Strength (at Break, TD)	30.0	MPa	ASTM D882
Elongation (at Break, MD)	1220.0	%	ASTM D882
Elongation (at Break, TD)	1440.0	%	ASTM D882
Tensile Modulus (1% Secant, MD)	180.0	MPa	ASTM D882
Tensile Modulus (1% Secant, TD)	200.0	MPa	ASTM D882
Dart Drop Impact Strength	90.0	g/F50	ASTM D1709
Elmendorf Tear Strength (MD)	120.0	gF	ASTM D1922
Elmendorf Tear Strength (TD)	340.0	gF	ASTM D1922

Control Properties

	Value	Units	Test Method / Conditions
Melt Flow Rate (at 190°C, 2.16kg)	2.7	g/10 min	ASTM D1238
Density	0.918	g/cm³	ASTM D1505

Note

Blown Film Properties:

• Film with 38 microns produce in a 40mm extruder and a blow‐up ratio of 2.2:1. (MD = extrusion direction and TD = transversal direction).