Properties
- Typical Properties
| Value | Units | Test Method / Conditions | |
| Viscosity | 25,000 - 30,000 | cps | — |
| Volume Resistivity | min. 1x 10^15 | Ω - cm | — |
| Dielectric Constant | 4 | — | — |
| Dielectric Strength | min. 4,000 | volts/mil | — |
| Glass Transition Temperature | min. 320 | °C | — |
| Hydrolytic Stability | Excellent | — | — |
| Useful Temperature Range | -55 to 330 | ºC | — |
| Thermal Stability | Good to +410 | °C | — |
Regulatory & Compliance
- Certifications & Compliance
Safety & Health
- Safety & Handling
- Use with adequate ventilation.
- Keep away from sparks and open flames.
- Avoid prolonged contact with skin and breathing of vapors.
- Wash with soap and water to remove from skin.
Storage & Handling
- Shelf Life
- 1 month at 25°C, 12 months at -40°C, 3 months at 5°C, 6 months at -10°C
- Suggested Handling
122-01UT is ready to use as supplied but can be thinned down with CMI 102-03 for printing optimization.
- Curing And Bonding
To use as an adhesive, apply b-staged adhesive to one part, carefully align parts to be bonded, apply uniform pressure to maintain location. Cure 60 minutes at 150°C followed by either 60 minutes at 250°C or 2 hours at 200°C. For better adhesion of the b-staged film to the first part, it is suggested to warm the part to 80°C. Cure times given are mass related, timing should start after adhesive and substrates reach curing temperature. For maximum chemical resistance a final cure temperature of 180°C is required. End user is advised to experimentally determine temperature and time best suited for individual applications.
- Storage
Shelf life up to 1 month at 25°C; or 3 months at 5°C; or 6 months at -10°C; or 12 months at -40°C. For extended storage -40°C is recommended. For syringe storage see syringe handling guidelines for recommendations on storage and maintaining homogeneity of material over long-term storage.