Knowde Enhanced TDS
Identification & Functionality
- Additives Included
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
Features & Benefits
- Materials Features
Applications & Uses
- Markets
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Color
- Flame Rating
- Flame Rating
- UL 94 V0
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Electrical Properties
- Flammability
- Other Properties
| Value | Units | Test Method / Conditions | |
| Tensile Strength | 160 | MPa | ASTM D 638 |
| Elongation at Break | 1.7 | % | ASTM D 638 |
| Tensile Modulus | 11000 | MPa | ASTM D638 |
| Flexural Strength | 220 | MPa | ASTM D790 |
| Flexural Modulus | 10000 | MPa | ASTM D 790 |
| Izod Impact notched (1/8 in) | 65 | J/m | ASTM D 256 |
| Izod Impact unnotched (1/8 in) | 480 | J/m | ASTM D 256 |
| Rockwell Hardness | 121 | Scale R | ASTM D 785 |
| Compressive Strength | 180 | MPa | ASTM D 695 |
| Value | Units | Test Method / Conditions | |
| Mold Shrinkage (MD) | 0.0025 | mm/mm | ASTM D 955 |
| Mold Shrinkage (TD) | 0.01 | mm/mm | ASTM D 955 |
| Density | 1570 | kg/m3 | ISO 1183 |
| Value | Units | Test Method / Conditions | |
| Coefficient of Thermal Expansion (MD) | 23 | E-6/K | ASTM D 696 |
| Deflection Temperature Under Load (264 psi) | 230 | °C | ASTM D 648 |
| Thickness tested | 0.8 | mm | — |
| Value | Units | Test Method / Conditions | |
| Dissipation Factor (1 MHz) | 0.002 | - | ASTM D 150 |
| Dielectric Strength (Short Time) | 16 | kV/mm | ASTM D 149 |
| Dielectric Constant (1 MHz) | 4 | - | ASTM D 150 |
| Arc Resistance | 120 | s | ASTM D 495 |
| Volume Resistivity | min. 1E15 | ohm.m | ASTM D 257 |
| Value | Units | Test Method / Conditions | |
| Flame rating | V-0 | - | UL 94 |
| Value | Units | Test Method / Conditions | |
| Water Absorption (24 hr) | 0.06 | % | ASTM D 570 |