LNP™ THERMOCOMP™ Compound OF008A

1 of 486 products in this brand
SABIC's Specialties Business LNP THERMOCOMP OF008A compound is based on branched Polyphenylene Sulfide (PPS) resin containing 40% glass fiber. This product does not contain PFAS intentionally added during SHPP’s manufacturing process and are not expected to contain unintentional PFAS impurities. Each user is responsible for evaluating the presence of unintentional PFAS impurities.

Polymer Name: Polyphenylene Sulfide (PPS)

Processing Methods: Injection Molding

Fillers Included: Glass Fiber

Technical Data Sheet

Popular SABIC's Specialties Business Products

View All SABIC's Specialties Business Products

Knowde Enhanced TDS

Identification & Functionality

Chemical Family

Polyphenylene Sulfide (PPS)

Fillers Included

Glass Fiber

Polymer Name

Polyphenylene Sulfide (PPS)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

High Performance Thermoplastics

Features & Benefits

Labeling Claims

No Added PFAS

Materials Features

Cost Effective,

High Modulus,

High Stiffness,

No Added PFAS

Applications & Uses

Markets

Building & Construction,

Consumer Goods,

Electrical & Electronics,

Personal Care,

Printing & Packaging

Applications

Consumer Goods — Appliances & Electronics

Building & Construction — Decorative Materials & Finishes

Artificial Turf

Electrical & Electronics — Devices & Assemblies

Consumer Electronics,

Displays

Consumer Goods — Lawn & Garden

Printing & Packaging — Packaging

Non-Food Consumer Packaging

Personal Care — Packaging & Accessories

Applicators & Accessories

Electrical & Electronics — Parts & Components

Connectors,

Switches & Relays

Consumer Goods — Sports & Recreation

Plastics & Elastomers End Uses

Appliances,

Building Materials,

Cell Phones,

Commercial Appliance,

Computer Components,

Consumer Applications,

Containers,

Displays,

Doors,

Electrical Components,

Electrical/Electronic Applications,

Garden Equipment,

Home Appliances,

Lawn Equipment,

Personal Accessories,

Pool Covers,

Sporting Goods,

Tablets,

Tarpaulins,

Turf Applications,

Windows

Plastics & Elastomers Processing Methods

Injection Molding

Resins and Compounds for Water Management Applications

SABIC’S specialty resins and compounds offer the water management industry design flexibility to produce products with longer lives and higher quality. Our materials are excellent candidates to replace metal and can provide weight reduction, corrosion resistance, high strength and stiffness or inherent lubricity depending on the application’s requirements.

  • Thermal resistance
  • Structural mechanical performance

In addition to mechanical requirements, applications for the water management industry need certification for potable water compliance according to national standards. SABIC has developed a dedicated potable water certified portfolio to help our customers accelerate their application development time to market.

SABIC Offerings Certified for Water Management Applications:

LNP™ THERMOCOMP™ Compound OF008A - Resins And Compounds For Water Management Applications

For applications that do not require potable water certification, SABIC’s Specialties portfolio includes a wide range of specialized thermoplastic compounds based on different base resins and fillers.

Properties

Flame Rating

UL 94 5VA,

UL 94 V0

Mechanical Properties
ValueUnitsTest Method / Conditions
Tensile Stress (Break, 5 mm/min) ¹¹160MPaISO 527
Tensile Stress (Break, 5 mm/min) ¹¹182MPaISO 527
Tensile Stress (Break, Type I, 5 mm/min) ¹¹178MPaASTM D638
Tensile Stress (Break) ¹¹160MPaISO 527
Tensile Stress (Break) ¹¹178MPaASTM D638
Tensile Strain (Break, 5 mm/min) ¹¹1.7%ISO 527
Tensile Strain (Break, 5 mm/min) ¹¹1.2%ISO 527
Tensile Strain (Break, Type I, 5 mm/min) ¹¹1.7%ASTM D638
Tensile Strain (Break) ¹¹1.7%ASTM D638
Tensile Strain (Break) ¹¹1.2%ISO 527
Flexural Stress (Break, 2 mm/min) ¹¹271MPaISO 178
Flexural Stress (Yield, 1.3 mm/min, 50 mm span) ¹¹248MPaASTM D790
Flexural Stress ¹¹248MPaASTM D790
Flexural Stress ¹¹190MPaISO 178
Flexural Modulus (at 1.3 mm/min, 50 mm span) ¹¹14260MPaASTM D790
Flexural Modulus (at 2 mm/min) ¹¹14000MPaISO 178
Flexural Modulus (at 2 mm/min) ¹¹13400MPaISO 178
Flexural Modulus ¹¹14260MPaASTM D790
Flexural Modulus ¹¹13400MPaISO 178
Flexural Stress (Yield, at 2 mm/min) ¹¹190MPaISO 178
Physical Properties
ValueUnitsTest Method / Conditions
Mold Shrinkage (on Tensile Bar, flow) ᵍ ¹¹0.15 - 0.25%SABIC method
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹0.2%ASTM D955
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹0.2 - 0.4%ISO 294
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹0.8%ASTM D955
Mold Shrinkage (xflow, 24 hrs) ᵍ ¹¹0.8 - 1.2%ISO 294
Density ¹¹1.65g/cm³ISO 1183
Density ¹¹1.68g/cm³ASTM D792
Wear Factor Washer ¹¹24010^-10 in^5-min/ft-lb-hrASTM D3702 Modified: Manual
Dynamic COF ¹¹0.41—ASTM D3702 Modified: Manual
Static COF ¹¹0.87—ASTM D3702 Modified: Manual
Thermal Properties
ValueUnitsTest Method / Conditions
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹0.0000261/°CISO 11359-2
Heat Deflection Temperature/Af (at 1.8 Mpa, Flatw 80*10*4, sp=64mm) ¹¹272°CISO 75/Af
Relative Temperature Index (Electrical) ᵖ ¹¹220°CUL 746B
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹200°CUL 746B
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹220°CUL 746B
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹261°CASTM D648
Coefficient of Thermal Expansion (at -40°C to 40°C, flow) ¹¹0.0000261/°CISO 11359-2
Electrical Properties
ValueUnitsTest Method / Conditions
Arc Resistance (Tungsten, PLC) ¹⁷5PLC CodeASTM D495
Comparative Tracking Index (UL, PLC) ¹⁷4PLC CodeUL 746A
Comparative Tracking Index (UL, PLC) ¹⁷2PLC CodeUL 746A
High Ampere Arc Ignition (PLC 4) ¹⁷min. 1.5mmUL 746A
High Voltage Arc Track Rate (PLC) ¹⁷1PLC CodeUL 746A
Hot Wire Ignition (PLC 0) ¹⁷min. 6mmUL 746A
Hot Wire Ignition (PLC 1) ¹⁷min. 3mmUL 746A
Hot Wire Ignition (PLC 2) ¹⁷min. 1.5mmUL 746A
Impact Properties
ValueUnitsTest Method / Conditions
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹21kJ/m²ISO 180/1U
Izod Impact (Unnotched, 80*10*4, at 23°C) ¹¹45kJ/m²ISO 180/1U
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹9kJ/m²ISO 180/1A
Izod Impact (Notched, 80*10*4, at 23°C) ¹¹6kJ/m²ISO 180/1A
Izod Impact (Unnotched, at 23°C) ¹¹587J/mASTM D4812
Izod Impact (Notched, at 23°C) ¹¹101J/mASTM D256
Injection Molding
ValueUnitsTest Method / Conditions
Drying Temperature ⁷120 - 150°C—
Drying Time ⁷4Hrs—
Melt Temperature ⁷315 - 320°C—
Front - Zone 3 Temperature ⁷330 - 345°C—
Middle - Zone 2 Temperature ⁷320 - 330°C—
Rear - Zone 1 Temperature ⁷305 - 315°C—
Mold Temperature ⁷140 - 165°C—
Back Pressure ⁷0.2 - 0.3MPa—
Screw Speed ⁷30 - 60rpm—
Flame Characteristics
ValueUnitsTest Method / Conditions
UL Recognized (94-5VA Flame Class Rating) ᵖmin. 3mmUL 94
UL Recognized (94V-0 Flame Class Rating) ᵖmin. 0.45mmUL 94
Note
  • ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.
  • ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.
  • ⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.
  • ¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
  • ¹⁷ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card. The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.
 

Regulatory & Compliance

Certifications & Compliance

UL 94

Packaging & Availability

Country Availability

Canada,

China (Mainland),

Mexico,

USA

Regional Availability
  • Americas
  • Asia
  • Europe
  • North America