Domamid® 6LVG30 300 BK99

Identification & Functionality

Chemical Family

Polyamides

Fillers Included

Glass Fiber

Polymer Name

Polyamide 6 (PA 6)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Applications & Uses

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Color

Black

Filler

Glass Fiber

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Modulus (1 mm/min)	9500 / 6200	MPa	ISO 527
Tensile Stress at Break (5 mm/min)	180 / 110	MPa	ISO 527
Tensile Strain at Break (5 mm/min)	4 / 7	%	ISO 527
Flexural Strength (5 mm/min)	270 / 175	MPa	ISO 178
Flexural Modulus (5 mm/min)	8000 / 4700	MPa	ISO 178
Charpy Notched Impact Strength (+23 °C)	12 / 25	kJ/m2	ISO 179/1eA
Charpy Notched Impact Strength (-30°C)	10 / -	kJ/m2	ISO 179/1eA
Charpy Unnotched Impact Strength (+23 °C)	80 / 85	kJ/m2	ISO 179/1eU
Charpy Unnotched Impact Strength (-30 °C)	70 / -	kJ/m2	ISO 179/1eU
Izod Notched Impact Strength (-30°C)	11 / -	kJ/m2	ISO 180/1A

Physical Properties

	Value	Units	Test Method / Conditions
Melt Volume Rate - MVR (275 °C/5.0 kg)	60	cm3/10 min	ISO 1133
Molding Shrinkage - Parallel (72 hrs, 23°C, 50% RH)	0.20 - 0.40	%	ISO 294-4 / 2577
Molding Shrinkage - Transverse (72 hrs, 23°C, 50% RH)	0.70 - 0.90	%	ISO 294-4 / 2577
Moisture Absorption (T=23°C / 50%RH)	1.9 - 2.3	%	ISO 62
Water Absorption (T=23°C / sat.)	6.3 - 6.9	%	ISO 62
Viscosity Number (96% H2SO4)	125	ml/g	ISO 307

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature - HDT/A (1.80 MPa)	205	°C	ISO 75
Heat Deflection Temperature - HDT/B (0.45 MPa)	215	°C	ISO 75

Processing Parameters

	Value	Units	Test Method / Conditions
Drying Time (with dew point of dried air < -30 °C)	2.0 - 4.0	h	—
Recommended Melt Temperature	250 - 290	°C	—
Recommended Mold Temperature	80 - 100	°C	—
Drying Temperature	75 - 85	°C	—