Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Plastics & Elastomers Processing Methods
Properties
- Flame Rating
- Flame Rating
- UL 94 HB
- Filler
- Glass Fiber
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Electrical Properties
- Flammability
- Processing Parameters
| Value | Units | Test Method / Conditions | |
| Tensile Modulus (1 mm/min) | 20500 / 12500 | MPa | ISO 527 |
| Tensile Stress at Break (5 mm/min) | 230 / 140 | MPa | ISO 527 |
| Tensile Strain at Break (5 mm/min) | 2.5 / 4.5 | % | ISO 527 |
| Flexural Strength (2 mm/min) | 350 / 210 | MPa | ISO 178 |
| Flexural Modulus (2 mm/min) | 17500 / 10500 | MPa | ISO 178 |
| Charpy Notched Impact Strength (+23 °C) | 15 / 22 | kJ/m2 | ISO 179/1eA |
| Charpy Unnotched Impact Strength (+23 °C) | 75 / 90 | kJ/m2 | ISO 179/1eU |
| Izod Notched Impact Strength (+23 °C) | 15 / 20 | kJ/m2 | ISO 180/1A |
| Izod Unnotched Impact Strength (+23 °C) | 70 / 85 | kJ/m2 | ISO 180/1U |
| Value | Units | Test Method / Conditions | |
| Molding Shrinkage - Parallel (72 hrs, 23°C, 50% RH) | 0.1 - 0.3 | % | ISO 294-4 / 2577 |
| Molding Shrinkage - Transverse (72 hrs, 23°C, 50% RH) | 0.3 - 0.5 | % | ISO 294-4 / 2577 |
| Water Absorption (T=23°C / sat.) | 4 | % | ISO 62 |
| Viscosity Number (96% H2SO4) | 125 | ml/g | ISO 307 |
| Value | Units | Test Method / Conditions | |
| Heat Deflection Temperature - HDT/A (1.80 MPa) | 210 | °C | ISO 75 |
| Heat Deflection Temperature - HDT/B (0.45 MPa) | 220 | °C | ISO 75 |
| Melting Point (DSC) | 221 | °C | ISO 11357-1 |
| Vicat Softening Temperature (50°C/h - 50N) | 210 | °C | ISO 306 |
| Value | Units | Test Method / Conditions | |
| Comparative Tracking Index - CTI (Solution A) | 500 | V | IEC 60112 |
| Value | Units | Test Method / Conditions | |
| Glow Wire Flammability Index - GWFI (1 - 3 mm) | 650 | °C | IEC 60695-2-12 |
| Flammability (0.8 mm) | HB | - | UL 94 |
| Value | Units | Test Method / Conditions | |
| Drying Time (with dew point of dried air < -30 °C) | 2.0 - 4.0 | h | - |
| Recommended Melt Temperature | 250 - 280 | °C | - |
| Recommended Mold Temperature | 90 - 100 | °C | - |
| Drying Temperature | 75 - 85 | °C | - |