LNP THERMOCOMP™ Compound - PF007 - SABIC's Specialty

Identification & Functionality

Features & Benefits

Labeling Claims: No Added PFAS
Materials Features: Cost Effective,
Good Mold Release,
Heat Stabilized,
High Modulus,
High Stiffness,
No Added PFAS

Applications & Uses

Markets: Building & Construction,
Consumer Goods,
Electrical & Electronics,
Personal Care,
Printing & Packaging
Applications: Consumer Goods — Appliances & Electronics
Building & Construction — Decorative Materials & Finishes
Artificial Turf
Electrical & Electronics — Devices & Assemblies
Consumer Electronics,
Displays
Consumer Goods — Lawn & Garden
Printing & Packaging — Packaging
Non-Food Consumer Packaging
Personal Care — Packaging & Accessories
Applicators & Accessories
Electrical & Electronics — Parts & Components
Connectors,
Switches & Relays
Consumer Goods — Sports & Recreation
Plastics & Elastomers End Uses: Appliances,
Building Materials,
Cell Phones,
Commercial Appliance,
Computer Components,
Consumer Applications,
Containers,
Displays,
Electrical Components,
Electrical/Electronic Applications,
Fishing Lines,
Fishing Nets,
Garden Equipment,
Home Appliances,
Lawn Equipment,
Personal Accessories,
Pool Covers,
Sporting Goods,
Tablets,
Tarpaulins,
Turf Applications
Plastics & Elastomers Processing Methods: Injection Molding

Properties

Flame Rating: UL 94 HB
Mechanical Properties
Physical Properties
Thermal Properties
Electrical Properties
Impact Properties
Injection Molding
Flame Characteristics
Note: ᵍ Measurements made from Laboratory test Coupon. Actual shrinkage may vary outside of range due to differences in processing conditions, equipment, part geometry and tool design. It is recommended that mold shrinkage studies be performed with surrogate or legacy tooling prior to cutting tools for new molded article.

ᵖ UL ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details, please see the UL Yellow Card.

ʳ UL Ratings shown on the technical datasheet might not cover the full range of thicknesses, colors and regions. For details, please see the UL Yellow Card.

⁷ Injection Molding parameters are only mentioned as general guidelines. These may not apply or may need adjustment in specific situations such as low shot sizes, large part molding, thin wall molding and gas-assist molding.

¹¹ The information stated on Technical Datasheets should be used as indicative only for material selection purposes and not be utilized as specification or used for part or tool design.

	Value	Units	Test Method / Conditions
Density ¹¹	1.42	g/cm³	ISO 1183
Density ¹¹	1.43	g/cm³	ASTM D792
Mold Shrinkage (flow, 24 hrs) ᵍ ¹¹	0.8	%	ASTM D955
Mold Shrinkage (on Tensile Bar, flow) ᵍ ¹¹	0.15 - 0.35	%	SABIC method
Water Absorption (at 23°C, saturated) ¹¹	6.2	%	ISO 62-1
Moisture Absorption (at 23°C, 50% RH) ¹¹	1.6	%	ISO 62

	Value	Units	Test Method / Conditions
Heat Deflection Temperature (at 1.82 MPa, 3.2mm, Unannealed) ¹¹	205	°C	ASTM D648
Relative Temperature Index (Electrical) ᵖ ¹¹	130	°C	UL 746B
Relative Temperature Index (Mechanical with impact) ᵖ ¹¹	70	°C	UL 746B
Relative Temperature Index (Mechanical without impact) ᵖ ¹¹	85	°C	UL 746B
Thermal Conductivity ¹¹	0.33	W/m-°C	ISO 8302
Coefficient of Thermal Expansion (at 23°C to 60°C, flow) ¹¹	0.000021	1/°C	ISO 11359-2
Coefficient of Thermal Expansion (at 23°C to 60°C, xflow) ¹¹	0.000081	1/°C	ISO 11359-2
Ball Pressure Test (at 123°C to 127°C) ¹¹	Pass	—	IEC 60695-10-2
Vicat Softening Temperature (Rate B/50) ¹¹	217	°C	ISO 306
Vicat Softening Temperature (Rate B/120) ¹¹	216	°C	ISO 306
Heat Deflection Temperature/Be (at 0.45MPa, Edgew 120104, sp=100mm) ¹¹	220	°C	ISO 75/Be
Heat Deflection Temperature/Ae (at 1.8 Mpa, Edgew 120104, sp=100mm) ¹¹	215	°C	ISO 75/Ae

	Value	Units	Test Method / Conditions
Volume Resistivity ¹¹	min. 1.E+16	Ω.cm	IEC 60093
Surface Resistivity (ROA) ¹¹	min. 1.E+16	Ω	IEC 60093
Dielectric Strength (in oil, at 3.2mm) ¹¹	20	kV/mm	IEC 60243-1
Relative Permittivity (1 MHz) ¹¹	3.4	—	IEC 60250
Dissipation Factor (at 50/60 Hz) ¹¹	0.0061	—	IEC 60250
Dissipation Factor (at at 1 MHz) ¹¹	0.016	—	IEC 60250
Comparative Tracking Index ʳ ¹¹	500	V	IEC 60112
Comparative Tracking Index (M) ʳ ¹¹	400	V	IEC 60112
Relative Permittivity (50/60 Hz) ¹¹	3.6	—	IEC 60250

	Value	Units	Test Method / Conditions
Izod Impact (Unnotched, at 23°C) ¹¹	1222	J/m	ASTM D4812
Izod Impact (Notched, 80104, at 23°C) ¹¹	16	kJ/m²	ISO 180/1A
Izod Impact (Notched, at 23°C) ¹¹	144	J/m	ASTM D256
Izod Impact (Notched, 80104, at -20°C) ¹¹	12	kJ/m²	ISO 180/1A
Izod Impact (Notched, 80104, at -30°C) ¹¹	11	kJ/m²	ISO 180/1A
Izod Impact (Notched, 80104, at -40°C) ¹¹	10	kJ/m²	ISO 180/1A
Charpy Impact (at 23°C, V-notch Edgew 80104 sp=62mm) ¹¹	15	kJ/m²	ISO 179/1eA
Charpy Impact (at -30°C, V-notch Edgew 80104 sp=62mm) ¹¹	12	kJ/m²	ISO 179/1eA
Charpy Impact (at 23°C, Unnotch Edgew 80104 sp=62mm) ¹¹	90	kJ/m²	ISO 179/1eU
Charpy Impact (at -30°C, Unnotch Edgew 80104 sp=62mm) ¹¹	85	kJ/m²	ISO 179/1eU

	Value	Units	Test Method / Conditions
UL Recognized (94HB Flame Class Rating) ᵖ	1.5	mm	UL 94
UL Compliant (94HB Flame Class Rating) ᵖ	0.75	mm	UL 94 by SABIC-IP
Glow Wire Flammability Index (passes at 650°C) ʳ ᵖ	2	mm	IEC 60695-2-12
Oxygen Index (LOI) ᵖ	27	%	ISO 4589
FMVSS Burning Speed (Thickness 2 mm) ᵖ	10	mm/min	FMVSS 302
FMVSS Burning Speed (Thickness 3 mm) ᵖ	5	mm/min	FMVSS 302