Value | Units | Test Method / Conditions | |
Tensile Modulus (1 mm/min) | 3200 | MPa | ISO 527 |
Tensile Stress at Break (5 mm/min) | 60 | MPa | ISO 527-2/1A |
Tensile Strain at Break (5 mm/min) | 25 | % | ISO 527 |
Flexural Strength (2 mm/min) | 105 | MPa | ISO 178 |
Flexural Modulus (2 mm/min) | 2900 | MPa | ISO 178 |
Charpy Notched Impact Strength (+23 °C) | 7 | kJ/m2 | ISO 179/1eA |
Charpy Unnotched Impact Strength (+23 °C) | NB | kJ/m2 | ISO 179/1eU |
Izod Notched Impact Strength (+23 °C) | 7 | kJ/m2 | ISO 180/1A |
Izod Unnotched Impact Strength (+23 °C) | NB | kJ/m2 | ISO 180/1U |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature - HDT/B (0.45 MPa) | 180 | °C | ISO 75 |
Melting Point (DSC) | 221 | °C | ISO 11357-1 |
Vicat Softening Temperature (50°C/h - 50N) | 200 | °C | ISO 306 |
Value | Units | Test Method / Conditions | |
Flammability (1.6 mm) | HB | Class | UL 94 |
Value | Units | Test Method / Conditions | |
Drying Time (with dew point of dried air < -30 °C) | 2.0 - 4.0 | h | - |
Recommended Melt Temperature | 230 - 260 | °C | - |
Drying Temperature | 75 - 85 | °C | - |