Econamid® AIR 6RC10H2 BK99

Identification & Functionality

Chemical Family

Polyamides

Fillers Included

Carbon Fiber

Polymer Name

Polyamide 6 (PA 6)

Plastics & Elastomers Functions

Resin

Technologies

Plastics

Product Families

Plastics — Engineering & Specialty Polymers

Polyamides

Features & Benefits

Materials Features

Heat Stabilized

Applications & Uses

Plastics & Elastomers Processing Methods

Injection Molding

Properties

Color

Black

Flame Rating

UL 94 HB

Flame Rating

UL 94 HB

Filler

Carbon Fiber

Mechanical Properties

	Value	Units	Test Method / Conditions
Tensile Modulus (1 mm/min)	9500 / 5000	MPa	ISO 527
Tensile Stress at Break (5 mm/min)	140 / 80	MPa	ISO 527
Tensile Strain at Break (5 mm/min)	3.2 / 8	%	ISO 527
Flexural Strength (2 mm/min)	170 / 90	MPa	ISO 178
Flexural Modulus (2 mm/min)	7500 / 4000	MPa	ISO 178
Charpy Notched Impact Strength (+23 °C)	5 / 11	kJ/m2	ISO 179/1eA
Charpy Unnotched Impact Strength (+23 °C)	40 / 70	kJ/m2	ISO 179/1eU

Physical Properties

	Value	Units	Test Method / Conditions
Molding Shrinkage - Parallel (72 hrs, 23°C, 50% RH)	0.30 - 0.50	%	ISO 294-4 / 2577
Molding Shrinkage - Transverse (72 hrs, 23°C, 50% RH)	0.75 - 1.05	%	ISO 294-4 / 2577

Thermal Properties

	Value	Units	Test Method / Conditions
Heat Deflection Temperature - HDT/A (1.80 MPa)	200	°C	ISO 75
Melting Point (DSC)	221	°C	ISO 11357-1

Flammability

	Value	Units	Test Method / Conditions
Flammability (0.8 mm)	HB	-	UL 94

Processing Parameters

	Value	Units	Test Method / Conditions
Drying Time (with dew point of dried air < -30 °C)	2.0 - 4.0	h	-
Recommended Melt Temperature	240 - 280	°C	-
Recommended Mold Temperature	80 - 110	°C	-
Drying Temperature	75 - 85	°C	-