Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Applications & Uses
- Plastics & Elastomers Processing Methods
Properties
- Filler
- Glass Fiber
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Flammability
- Processing Parameters
Value | Units | Test Method / Conditions | |
Tensile Modulus (1 mm/min) | 10500 / 5500 | MPa | ISO 527 |
Tensile Stress at Break (5 mm/min) | 150 / 90 | MPa | ISO 527 |
Tensile Strain at Break (5 mm/min) | 2.5 / 6.0 | % | ISO 527 |
Flexural Strength (5 mm/min) | 230 / 140 | MPa | ISO 178 |
Flexural Modulus (5 mm/min) | 9000 / 5000 | MPa | ISO 178 |
Charpy Notched Impact Strength (+23 °C) | 9 / 19 | kJ/m2 | ISO 179/1eA |
Charpy Notched Impact Strength (-30°C) | 6 / 7 | kJ/m2 | ISO 179/1eA |
Charpy Unnotched Impact Strength (+23 °C) | 62 / 75 | kJ/m2 | ISO 179/1eU |
Charpy Unnotched Impact Strength (-30 °C) | 55 / 60 | kJ/m2 | ISO 179/1eU |
Value | Units | Test Method / Conditions | |
Molding Shrinkage - Parallel (72 hrs, 23°C, 50% RH) | 0.25 - 0.45 | % | ISO 294-4 / 2577 |
Molding Shrinkage - Transverse (72 hrs, 23°C, 50% RH) | 0.75 - 0.95 | % | ISO 294-4 / 2577 |
Water Absorption (T=23°C / sat.) | 2 | % | ISO 62 |
Viscosity Number (96% H2SO4) | 135 | ml/g | ISO 307 |
Value | Units | Test Method / Conditions | |
Heat Deflection Temperature - HDT/A (1.80 MPa) | 210 | °C | ISO 75 |
Heat Deflection Temperature - HDT/B (0.45 MPa) | 220 | °C | ISO 75 |
Value | Units | Test Method / Conditions | |
Glow Wire Flammability Index - GWFI (1 - 3 mm) | 650 | °C | IEC 60695-2-12 |
Value | Units | Test Method / Conditions | |
Drying Time (with dew point of dried air < -30 °C) | 2.0 - 4.0 | h | - |
Recommended Melt Temperature | 250 - 290 | °C | - |
Recommended Mold Temperature | 80 - 100 | °C | - |
Drying Temperature | 75 - 85 | °C | - |