Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Basis
- Infiltration resin for porous parts
- Technologies
- Product Families
Features & Benefits
- Materials Features
- Properties
very low viscosity
good wet-out characteristics
very long flow paths
Applications & Uses
- Plastics & Elastomers Processing Methods
- Applications
Infiltration of printed porous parts
- Processing Instructions
The temperature of material and processing should be between 18 and 25° C. The mixing of resin and hardener should be made intensively and at room temperature.
Properties
- Typical Properties
| Value | Units | Test Method / Conditions | |
| Shore hardness | 85 ± 3 | Shore D | DIN ISO 7619-1 |
| Viscosity (25°C) | 250 ± 50 | mPa.s | - |
| Compressive Strength | 95 ± 5 | MPa | EN ISO 604 |
| Density (20°C) | 1,13 ± 0,02 | g/cm3 | - |
| Flexural elongation at break | 5.9 ± 0.1 | % | EN ISO 178 |
| Pot Life (200g/20°C) | 300 - 400 | minutes | - |
| Flexural modulus | 3400 ± 300 | MPa | EN ISO 178 |
| Curing time at RT | 36 - 48 | Hrs | - |
| Flexural strength | 125 ± 1.2 | MPa | EN ISO 178 |
| Heat resistance (HDT) | 79 ± 3 | °C | DIN EN ISO 75 B |
| Impact resistance (Charpy) | 60 ± 6 | kJ/m2 | EN ISO 179 |
Packaging & Availability
- Packages
0,150 kg / 1,200 kg
- Availability
At bigger quantities of >500g the working time will be clearly shorte
For ebalta IH 16 are 3 different hardeners available. IH 16 hardener slow: pot life 300 - 400 min. IH 16 hardener fast: pot life 50 - 60 min. IH 16 hardener very fast: pot life 15 - 25 min. (for machine application)
Storage & Handling
- Storing
At appropriate storage 18-25°C. Occuring crystallization due to disadvantageous storage conditions can be made return by warming up the material at approx. 60° C for some hours. Opened containers should be closed immediately after use and be protected against moisture. This material should be used up as soon as possible. Shelf life is indicated on the labels