Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
Applications & Uses
- Applications
- Plastics & Elastomers Processing Methods
Properties
- Flame Rating
- Flame Rating
- UL 94 HB
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Flammability
- Processing Information (Injection Molding)
| Value | Units | Test Method / Conditions | |
| Elongation at Break (23°C/50% Relative Humidity, 5 mm/min) | min. 5 | % | ASTM D 638 |
| Elongation at Break (23°C/50% Relative Humidity, 50 mm/min) | min. 5 | % | ISO 527-1,2 |
| Tensile Modulus (23°C/50% Relative Humidity, 5 mm/min) | 232000 | psi | ASTM D 638 |
| Tensile Modulus (23°C/50% Relative Humidity, 1 mm/min) | 1600 | MPa | ISO 527-1,2 |
| Yield Stress (23°C/50% Relative Humidity, 5 mm/min) | 32 | MPa | ASTM D 638 |
| Yield Stress (23°C/50% Relative Humidity, 50 mm/min) | 35 | MPa | ISO 527-1,2 |
| Flexural Modulus (23°C/50% Relative Humidity, 1.3 mm/min) | 249000 | psi | ASTM D 790 |
| Flexural Modulus (23°C/50% Relative Humidity, 2 mm/min) | 1720 | MPa | ISO 178 |
| Izod Notched Impact Strength (-22°F (-30°C), 50% Relative Humidity, 3.2mm, 1/8”) | 190 | J/m | ASTM D 256 |
| Izod Notched Impact Strength (73°F (23°C), 50% Relative Humidity, 6.4mm,1/4”) | 365 | J/m | ASTM D 256 |
| Izod Notched Impact Strength (23°C (73°F), 50% Relative Humidity) | 28 | kJ/m2 | ISO 180-1A |
| Izod Notched Impact Strength (-30°C (-22°F), 50% Relative Humidity) | 21 | kJ/m2 | ISO 180-1A |
| Ball Indentation Hardness (23°C/50% Relative Humidity) | 72 | N/mm2 | ISO 2039-1 |
| Value | Units | Test Method / Conditions | |
| Melt Flow Rate - MFR (230°C, 3.8Kg) | 4 | g/10min | ASTM D1238 |
| Melt Volume Flow Rate - MVFR (220°C, 10Kg) | 14 | cm3/10min | ISO 1133 |
| Yellow Index - YI (23°C) | 31 | — | E313 |
| Residual Monomers (23°C) | 0.03 | % | Lab - CG |
| Butadiene Content (23°C) | 27 | % | Lab - IR |
| Density (25°C) | 1.02 | g/cm3 | ISO 1183-1 |
| Value | Units | Test Method / Conditions | |
| Vicat Softening Temperature (50N, 50°C/h) | 199 | ºF | ASTM D 1525 |
| Vicat Softening Temperature (B50, 50°C/h) | 93 | °C | ISO 306 |
| Value | Units | Test Method / Conditions | |
| Burning Rate (US-FMVSS, 250X105X2mm) | 60 | mm/min | ISO 3795 |
| Burning Behavior (1.6 mm) | HB Class | — | UL 94 |
| Burning Behavior (1.6 mm) | HB | Class | UL 94 |
| Glow Wire Test - GWFI (2.0 mm) | 700 | °C | IEC 60695-2-12 |
| Value | Units | Test Method / Conditions | |
| Mold Temperature | 70 | °C | ISO 294 |
| Injection Velocity | 240 | mm/s | ISO 294 |
| Melt Temperature | 240 | °C | ISO 294 |
Regulatory & Compliance
- Certifications & Compliance
Packaging & Availability
- Regional Availability