Knowde Enhanced TDS
Identification & Functionality
- Chemical Family
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
- Processing Method
Injection Molding
Applications & Uses
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
- Uses
General Purpose
Properties
- Flame Rating
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Flammability
- Processing Information (Injection Molding)
- Impact Properties
| Value | Units | Test Method / Conditions | |
| Flexural Modulus | 2200 | MPa | ASTM D790 |
| Flexural Strength | 68 | Mpa | ASTM D790 |
| Tensile Elongation (at Break) | 20 | % | ASTM D638 |
| Tensile Elongation (at Yield) | 2 | % | ASTM D638 |
| Tensile Modulus | 2130 | MPa | ASTM D638 |
| Tensile Strength (at Break) | 31 | MPa | ASTM D638 |
| Tensile Strength (at Yield) | 40 | MPa | ASTM D638 |
| Value | Units | Test Method / Conditions | |
| Density | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass Flow Rate | 5.6 | g/10 min | ASTM D1238 |
| Melt Volume Flow Rate | 18 | cm³/10min | ISO 1133 |
| Value | Units | Test Method / Conditions | |
| Coefficient of Linear Thermal Expansion Flow (at -40 to 40°C) | 8.85E-5 | cm/cm/°C | ASTM D1525 |
| Coefficient of Linear Thermal Expansion Transverse (at -40 to 40°C) | 8.85E-5 | cm/cm/°C | ASTM D1525 |
| Deflection Temperature Under Load (at 0.45 MPa, Unannealed, 3.2 mm) | 96 | °C | D648 |
| Deflection Temperature Under Load (at 1.8 MPa, Unannealed, 3.2 mm) | 82 | °C | ASTM D256 |
| Relative Thermal Index | 60 | °C | UL 746 |
| Vicat Softening Temperature | 98 | °C | ASTM D3763 |
| Value | Units | Test Method / Conditions | |
| Flame Rating (at 1.5mm) | HB | — | UL 94 |
| Value | Units | Test Method / Conditions | |
| Back Pressure | 0.3 - 0.7 | Mpa | — |
| Drying Temperature | 80 - 95 | °C | — |
| Drying Time | 2 - 4 | hours | — |
| Front Temperature | 215 - 240 | °C | — |
| Middle Temperature | 205 - 225 | °C | — |
| Mold Temperature | 50 - 70 | °C | — |
| Nozzle Temperature | 220 - 260 | °C | — |
| Processing Melt Temperature | 220 - 260 | °C | — |
| Rear Temperature | 190 - 210 | °C | — |
| Screw Speed | 30 - 60 | rpm | — |
| Suggested Maximum Moisture | 0.1 | % | — |
| Suggested Shot Size | 50 - 70 | % | — |
| Vent Depth | 0.038 - 0.051 | mm | — |
| Value | Units | Test Method / Conditions | |
| Dart Impact | 30 | J | ASTM D3763 |
| Notched Izod Impact | 290 | J/m | ASTM D256 |
Regulatory & Compliance
- Certifications & Compliance
Packaging & Availability
- Country Availability
- Regional Availability
- Availability
- Africa and Middle East
- Europe
- North America
- Latin America
- Asia Pacific