Knowde Enhanced TDS
Identification & Functionality
- Fillers Included
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Flame Rating
- Flame Rating
- IEC 60695-11-10 HB
- Mechanical Properties
- Physical Properties
- Thermal Properties
- Electrical Properties
- Other Properties
Value | Units | Test Method / Conditions | |
Tensile Strength | 125 | MPa | ISO 527 |
Tensile Modulus | 10000 | MPa | ISO 527 |
Strain at break | 1.5 | % | ISO 527 |
Flexural modulus, 23° | 9400 | MPa | ISO 178 |
Charpy notched impact strength (+23°) | 5 | kJ/m2 | ISO 179/1eA |
Charpy impact strength (+23°) | 25 | kJ/m2 | ISO 179/1eU |
Izod notched impact strength, +23° | 5.5 | kJ/m2 | ISO 180/1A |
Ball indentation hardness | 230 | MPa | ISO 2039-1 |
Value | Units | Test Method / Conditions | |
Melt Flow Index - MFI (190°C/2.16 kg) | 3 | g/10 min | ISO 1133 |
Melt Mass Flow Rate - MFR (190°C/2.16 kg) | 3 | g/10 min | ASTM D1238 |
Melt Volume Flow Rate - MVR (190°C/2.16 kg) | 2.5 | cm3/10 min | ISO 1133 |
Molding Shrinkage - Paralell (60×60×2 mm) | 0 | % | ISO 294-4 |
Molding Shrinkage - Paralell (60×60×2 mm) | 7/1 | % | ISO 294-4 |
Molding Shrinkage - Paralell (60×60×2 mm) | 3 | % | ISO 294-4 |
Molding shrinkage - parallel | 0.7 | % | ISO 294-4, 2577 |
Molding shrinkage - normal | 1.3 | % | ISO 294-4, 2577 |
Water Absorption (23/sat.) | 0.8 | % | ISO 62 |
Moisture Absorption (23°C/50% RH) | 0.17 | % | ISO 62 |
Density | 1630 | kg/m3 | ISO 1183 |
Value | Units | Test Method / Conditions | |
Coefficient of Linear Thermal Expansion (parallel) | 40 | E-6/K | ISO 11359-1/-2 |
Coefficient of Linear Thermal Expansion (normal) | 80 | E-6/K | ISO 11359-1/-2 |
Delfection Temperature Under Load (1.8 MPa) | 160 | °C | ISO 75-1,-2 |
Temperature of deflection under load (1.80 Mpa) | 160 | °C | ISO 75-1/-2 |
Melting Point (DSC) | 167 | °C | ISO 11357-1-3 |
Vicat Softening Temperature (50 N) | 160 | °C | ISO 306 |
Melting temperature (10°C/min) | 167 | °C | ISO 11357-1/-3 |
Thickness tested | 3.2 | mm | - |
Vicat softening temperature | 160 | °C | ISO 306 |
Burning Behavior at thickness | HB | class | IEC 60695-11-10 |
Value | Units | Test Method / Conditions | |
Comparative Tracking Index - CTI | 600 | V | UL 746 |
Surface Resistivity | 1.00E+13 | ohm | IEC 60093 |
Volume Resistivity | 100000000000000.0 | ohm.m | ASTM D 257 |
Value | Units | Test Method / Conditions | |
Water absorption | 0.8 | % | Sim. to ISO 62 |
Humidity absorption | 0.17 | % | Sim. to ISO 62 |