Knowde Enhanced TDS
Identification & Functionality
- Polymer Name
- Plastics & Elastomers Functions
- Technologies
- Product Families
Features & Benefits
- Materials Features
Applications & Uses
- Applications
- Plastics & Elastomers End Uses
- Plastics & Elastomers Processing Methods
Properties
- Flame Rating
- Flame Rating
- IEC 60695-11-10 HB
- Physical Properties
- Mechanical Properties
- Thermal Properties
- Electrical Properties
- Other Properties
| Value | Units | Test Method / Conditions | |
| Melt Flow Index - MFI (190°C/2.16 kg) | 13 | g/10 min | ASTM D 1238 |
| Melt Mass Flow Rate - MFR (190°C/2.16 kg) | 13 | g/10 min | ASTM D1238 |
| Melt Volume Flow Rate - MVR (190°C/2.16 kg) | 11.5 | cm3/10 min | ISO 1133 |
| Molding Shrinkage - Paralell (60×60×2 mm) | 2 | % | ISO 294-4 |
| Molding Shrinkage - Paralell (60×60×2 mm) | 0/- | % | ISO 294-4 |
| Molding shrinkage - parallel | 2 | % | ISO 294-4, 2577 |
| Water Absorption (23/sat.) | 0.8 | % | ISO 62 |
| Moisture Absorption (23°C/50% RH) | 0.2 | % | ISO 62 |
| Density | 1410 | kg/m3 | ASTM D 792 |
| Value | Units | Test Method / Conditions | |
| Tensile Modulus | 2750 | MPa | ISO 527 |
| Yield stress | 63 | MPa | ISO 527 |
| Yield strain | 10 | % | ISO 527 |
| Strain at break | 25 | % | ISO 527 |
| Flexural modulus, 23° | 2500 | MPa | ISO 178 |
| Charpy notched impact strength (+23°) | 6 | kJ/m2 | ISO 179/1eA |
| Charpy notched impact strength (-30°) | 5.5 | kJ/m2 | ISO 179/1eA |
| Charpy impact strength (+23°) | 170 | kJ/m2 | ISO 179/1eU |
| Charpy impact strength (-30°) | 140 | kJ/m2 | ISO 179/1eU |
| Izod notched impact strength, +23° | 6 | kJ/m2 | ISO 180/1A |
| Ball indentation hardness | 160 | MPa | ISO 2039-1 |
| Value | Units | Test Method / Conditions | |
| Coefficient of Linear Thermal Expansion (parallel) | 110 | E-6/K | ISO 11359-1/-2 |
| Delfection Temperature Under Load (1.8 MPa) | 115 | °C | ISO 75-1,-2 |
| Temperature of deflection under load (1.80 Mpa) | 115 | °C | ISO 75-1/-2 |
| Melting Point (DSC) | 167 | °C | ISO 11357-1-3 |
| Vicat Softening Temperature (50 N) | 150 | °C | ISO 306 |
| Melting temperature (10°C/min) | 167 | °C | ISO 11357-1/-3 |
| Thickness tested | 3.2 | mm | — |
| Vicat softening temperature | 150 | °C | ISO 306 |
| Burning Behavior at thickness | HB | class | IEC 60695-11-10 |
| Value | Units | Test Method / Conditions | |
| Comparative Tracking Index - CTI | 600 | V | UL 746 |
| Surface Resistivity | 1.00E+14 | ohm | IEC 60093 |
| Volume Resistivity | 1.0e+15 | ohm.m | ASTM D 257 |
| Value | Units | Test Method / Conditions | |
| Water absorption | 0.8 | % | Sim. to ISO 62 |
| Humidity absorption | 0.2 | % | Sim. to ISO 62 |
Packaging & Availability
- Country Availability
- Regional Availability